LG Chemical LUCON CP-4201F Conductive Thermoplastic, Flame Retardant
| Category | Polymer , Thermoplastic |
| Manufacturer | LG Chemical |
| Trade Name | LUCON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUCON CP-4201F Conductive Thermoplastic, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solving problems associated with build-up of electrostatic charges, electrostatic discharge, and electromagnetic interference. These materials span the surface resistivity spectrum from antistatic through conductive to EMI shielding (100-1012O).Applications: I.C. tray, wafer carrier, I.C. magazine, notebook PC case, home appliance part, LCD cassette trayInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | ASTM D785 |
| Tensile Strength at Break | 118 MPa | 17100 psi | ASTM D638 |
| Elongation at Break | <= 10 % | <= 10 % | ASTM D638 |
| Flexural Strength | 177 MPa | 25700 psi | ASTM D790 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | >= 0.250 W/m-K | >= 1.74 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm | 1.00e+8 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+8 ohm | 1.00e+8 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 300 °C | 500 - 572 °F | |
| Middle Barrel Temperature | 270 - 320 °C | 518 - 608 °F | |
| Front Barrel Temperature | 275 - 320 °C | 527 - 608 °F | |
| Nozzle Temperature | 275 - 320 °C | 527 - 608 °F | |
| Melt Temperature | 280 - 320 °C | 536 - 608 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 49.03 - 78.45 MPa | 7111 - 11380 psi | Second |
| 68.65 - 88.26 MPa | 9957 - 12800 psi | First | |
| Back Pressure | 0.000 - 1.96 MPa | 0.000 - 284 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- Precision Polymer Engineering J80P Butyl Rubber
- SABIC Innovative Plastics Cycolac® G366 ABS (Europe-Africa-Middle East)
- Nilit FRIANYL A63 W Nylon 6.6 for injection molding
- PolyOne Edgetek® PS-20GF/000 Polybutylene Terephthalate (PBT), Glass Filled (discontinued **)
- Industeel CREUSABRO® 4000 High Wear Resistant Steel
- Unifrax Fiberfrax® Long Staple Medium AZS Large-Diameter Fiber
- Polyram Bondyram® 5108 Maleic Anhydride Modified High Density Polyethylene
- A. Schulman POLYBLAK™ 4651SF Universal Black Color Concentrate, 50% Carbon Black in EVA
- A. Schulman POLYBATCH™ White 8000 AP Concentrate Based In LDPE
Copyright © lookpolymers.com All Rights Reserved