LG Chemical LI-943 ASA Resin  (discontinued **)

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LI-943 ASA Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Heat resistance, Excellent weather resistance, Well balanced mechanical properties, Superior chemical resistance, Good thermal aging stability, Good moldability and processability, Applications include side mirror housing, and trim panel
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 5.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
5.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength, Yield 41.0 MPa
5950 psi
50 mm/min; ASTM D638
Elongation at Break 35 %
35 %
50 mm/min; ASTM D638
Modulus of Elasticity 1.81 GPa
263 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 71.0 MPa
10300 psi
50 mm/min; ASTM D790
Flexural Modulus 2.21 GPa
321 ksi
15 mm/min; ASTM D790
Izod Impact, Notched 1.40 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
2.62 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
ASTM D256
1.80 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
3.37 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 91.0 °C

@Thickness 6.35 mm
196 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Vicat Softening Point 111 °C
232 °F
1000 g; ASTM D1525
Flammability, UL94 HB
HB
1/8 in
HB
HB
1/16 in