Dow Corning SILASTIC® 9252/250P PARTS A&B
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Dow Corning |
| Trade Name | SILASTIC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Corning SILASTIC® 9252/250P PARTS A&B.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Dow Corning
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc @Temperature 25.0 °C |
1.09 g/cc @Temperature 77.0 °F |
|
| Solids Content | 100 % | 100 % | |
| Viscosity | 25000 cP | 25000 cP | mixing, dynamic |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 5.00 MPa | 725 psi | |
| Elongation at Break | 450 % | 450 % | |
| Tear Strength | 7.01 kN/m | 40.0 pli |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.80e+15 ohm-cm | 4.80e+15 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 4320 min | 4320 min | |
| Shelf Life | 15.0 Month | 15.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | translucent | |
| Gel Hardness (Grams/Penetration) | 33 | |
| Mix Ratio (X:1) | 10 | Base to Catalyst |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXD104R PC
- LyondellBasell Adsylâ„¢ 5C37F Thermoplastic Olefin Resin
- LG Chemical EM600 Impact modifier for Engineering Plastics
- H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3)
- Zhejiang Juner 201-G20 20% Glass Fibre Reinforced
- A. Schulman ComAlloy® E-17036 Glass Fiber Reinforced High Heat Polycarbonate
- China-Yixing Longly Refractories Load Bearing Board Corundum-Mullite
- Carpenter Custom Age 625 PLUS® Nickel-Base Alloy, Aged 732°C (1350°F)/4hr/AC
- LG Chemical IM812 Acrylic impact modifier
Copyright © lookpolymers.com All Rights Reserved