LG Chemical KEYFLEX BT 3140D Ester Type TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | LG Chemical |
| Trade Name | KEYFLEX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical KEYFLEX BT 3140D Ester Type TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, TPC-ET, Specialty, Low Melting Temperature, Low ModulusApplication: Masterbatch Carrier, Cable Compound BaseCAS: 37282-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Molecular Weight | 458.458 g/mol | 458.458 g/mol | |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| 0.010 | 0.010 | Extrusion Molding | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength at Break | 29.1 MPa @Thickness 2.00 mm |
4220 psi @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Elongation at Break | 700 % @Thickness 2.00 mm |
700 % @Thickness 0.0787 in |
50mm/min; ASTM D638 |
| Flexural Modulus | 0.0539 GPa @Thickness 6.40 mm |
7.82 ksi @Thickness 0.252 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature -40.0 °C |
NB @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 °C | 302 °F | Peak |
| Boiling Point | 140 - 230 °C | 284 - 446 °F | |
| Flash Point | 300 - 340 °C | 572 - 644 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 26.0 kV/mm @Thickness 1.00 mm |
660 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| Middle Barrel Temperature | 170 - 190 °C | 338 - 374 °F | Injection Molding |
| Front Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Nozzle Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| Zone 1 | 160 - 180 °C | 320 - 356 °F | Extrusion Molding |
| Zone 2 | 170 - 190 °C | 338 - 374 °F | Extrusion Molding |
| Zone 3 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Zone 4 | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Adapter Temperature | 180 - 200 °C | 356 - 392 °F | Extrusion Molding |
| Die Temperature | 170 - 210 °C | 338 - 410 °F | Extrusion Molding |
| Melt Temperature | 150 - 200 °C | 302 - 392 °F | Injection Molding |
| 150 - 200 °C | 302 - 392 °F | Extrusion Molding | |
| Mold Temperature | 10.0 - 35.0 °C | 50.0 - 95.0 °F | Injection Molding |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding |
| 80.0 - 90.0 °C | 176 - 194 °F | Extrusion Molding | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| 3.00 - 4.00 hour | 3.00 - 4.00 hour | Extrusion Molding |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 20-0778/BK Polyphthalamide, with glass fiber and PTFE
- Kolon KOPA® KN133G15 G/F Reinforced Nylon 6
- Teknor Apex APEX® 1700-80 Polyvinyl Chloride, Flexible
- SMAC CABLE® 2521S-10-08 Damping Material
- Toyobo Zylon® HM Poly(p-phenylene-2,6-benzobisoxazole) Fiber
- Eastman Tenite Butyrate 576E3720010 Clear, Trsp Cellulose Acetate Butyrate
- ChevronTexaco ISO 15 Handy Oil
- AKG Polymers Vision PP PPH TC3004 Polypropylene Homopolymer Compound
- Solvay Specialty Polymers Veradel® AG-330 Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved