LATI Latamid 66 H2 G/25 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/25 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0085 - 0.0115 cm/cm
0.0085 - 0.0115 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa

@Temperature 150 °C
 11600 psi

@Temperature 302 °F
90.0 MPa

@Temperature 120 °C
 13100 psi

@Temperature 248 °F
100 MPa

@Temperature 90.0 °C
 14500 psi

@Temperature 194 °F
125 MPa

@Temperature 60.0 °C
 18100 psi

@Temperature 140 °F
160 MPa

@Temperature 23.0 °C
 23200 psi

@Temperature 73.4 °F
Elongation at Break 3.4 %

@Temperature 23.0 °C
 3.4 %

@Temperature 73.4 °F
4.2 %

@Temperature 60.0 °C
 4.2 %

@Temperature 140 °F
5.9 %

@Temperature 90.0 °C
 5.9 %

@Temperature 194 °F
6.2 %

@Temperature 120 °C
 6.2 %

@Temperature 248 °F
6.7 %

@Temperature 150 °C
 6.7 %

@Temperature 302 °F
Tensile Modulus 3.60 GPa

@Temperature 150 °C
 522 ksi

@Temperature 302 °F
4.80 GPa

@Temperature 120 °C
 696 ksi

@Temperature 248 °F
6.80 GPa

@Temperature 90.0 °C
 986 ksi

@Temperature 194 °F
8.10 GPa

@Temperature 60.0 °C
 1170 ksi

@Temperature 140 °F
8.90 GPa

@Temperature 23.0 °C
 1290 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 27 %
27 %
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa