LATI Lasulf G/15 PSU, 15% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 20% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Lasulf
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Lasulf G/15 PSU, 15% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polysulfone (PSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stabilityAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0045 cm/cm
0.0020 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0085 cm/cm
0.0065 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
<br>@Temperature 150 °C
 7250 psi
<br>@Temperature 302 °F
65.0 MPa
<br>@Temperature 120 °C
 9430 psi
<br>@Temperature 248 °F
75.0 MPa
<br>@Temperature 90.0 °C
 10900 psi
<br>@Temperature 194 °F
80.0 MPa
<br>@Temperature 60.0 °C
 11600 psi
<br>@Temperature 140 °F
90.0 MPa
<br>@Temperature 23.0 °C
 13100 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.3 %
<br>@Temperature 150 °C
 2.3 %
<br>@Temperature 302 °F
2.4 %
<br>@Temperature 90.0 °C
 2.4 %
<br>@Temperature 194 °F
2.4 %
<br>@Temperature 120 °C
 2.4 %
<br>@Temperature 248 °F
2.5 %
<br>@Temperature 60.0 °C
 2.5 %
<br>@Temperature 140 °F
2.7 %
<br>@Temperature 23.0 °C
 2.7 %
<br>@Temperature 73.4 °F
Tensile Modulus 4.70 GPa
<br>@Temperature 150 °C
 682 ksi
<br>@Temperature 302 °F
5.10 GPa
<br>@Temperature 120 °C
 740 ksi
<br>@Temperature 248 °F
5.20 GPa
<br>@Temperature 90.0 °C
 754 ksi
<br>@Temperature 194 °F
5.30 GPa
<br>@Temperature 60.0 °C
 769 ksi
<br>@Temperature 140 °F
5.50 GPa
<br>@Temperature 23.0 °C
 798 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
<br>@Temperature 23.0 °C
 14.3 ft-lb/in²
<br>@Temperature 73.4 °F
4.00 J/cm²
<br>@Temperature -20.0 °C
 19.0 ft-lb/in²
<br>@Temperature -4.00 °F
Charpy Impact, Notched 0.350 J/cm²
<br>@Temperature 23.0 °C
 1.67 ft-lb/in²
<br>@Temperature 73.4 °F
0.350 J/cm²
<br>@Temperature -20.0 °C
 1.67 ft-lb/in²
<br>@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 160 °C
320 °F
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
Vicat Softening Point 185 °C
<br>@Load 5.00 kg
 365 °F
<br>@Load 11.0 lb
Flammability, UL94 V-1
<br>@Thickness 1.50 mm
 V-1
<br>@Thickness 0.0591 in
V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
Oxygen Index 35 %
35 %
Glow Wire Test 960 °C
<br>@Thickness 1.00 mm
 1760 °F
<br>@Thickness 0.0394 in
 GWFI/GWT
960 °C
<br>@Thickness 2.00 mm
 1760 °F
<br>@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 125 V
125 V
A solution
Processing Properties Metric English Comments
Melt Temperature 300 - 330 °C
572 - 626 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 110 - 130 °C
<br>@Time 10800 sec
 230 - 266 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa