LATI Larton K/40 HM PPS, 40% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton K/40 HM PPS, 40% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Carbon fiber. High tensile modulus. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Temperature 150 °C
 14500 psi

@Temperature 302 °F
120 MPa

@Temperature 120 °C
 17400 psi

@Temperature 248 °F
145 MPa

@Temperature 90.0 °C
 21000 psi

@Temperature 194 °F
160 MPa

@Temperature 60.0 °C
 23200 psi

@Temperature 140 °F
175 MPa

@Temperature 23.0 °C
 25400 psi

@Temperature 73.4 °F
Elongation at Break 0.40 %

@Temperature 23.0 °C
 0.40 %

@Temperature 73.4 °F
0.50 %

@Temperature 60.0 °C
 0.50 %

@Temperature 140 °F
0.80 %

@Temperature 90.0 °C
 0.80 %

@Temperature 194 °F
1.0 %

@Temperature 120 °C
 1.0 %

@Temperature 248 °F
1.2 %

@Temperature 150 °C
 1.2 %

@Temperature 302 °F
Tensile Modulus 15.0 GPa

@Temperature 150 °C
 2180 ksi

@Temperature 302 °F
22.0 GPa

@Temperature 120 °C
 3190 ksi

@Temperature 248 °F
39.0 GPa

@Temperature 90.0 °C
 5660 ksi

@Temperature 194 °F
42.0 GPa

@Temperature 60.0 °C
 6090 ksi

@Temperature 140 °F
45.0 GPa

@Temperature 23.0 °C
 6530 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.00 J/cm²
4.76 ft-lb/in²
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 120 ohm-cm
120 ohm-cm
Surface Resistance 50 ohm
50 ohm
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa