LATI Larton K/30 PPS, 30% Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton K/30 PPS, 30% Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
85.0 MPa

@Temperature 120 °C
 12300 psi

@Temperature 248 °F
130 MPa

@Temperature 90.0 °C
 18900 psi

@Temperature 194 °F
165 MPa

@Temperature 60.0 °C
 23900 psi

@Temperature 140 °F
185 MPa

@Temperature 23.0 °C
 26800 psi

@Temperature 73.4 °F
Elongation at Break 0.80 %

@Temperature 23.0 °C
 0.80 %

@Temperature 73.4 °F
0.90 %

@Temperature 60.0 °C
 0.90 %

@Temperature 140 °F
1.3 %

@Temperature 90.0 °C
 1.3 %

@Temperature 194 °F
1.6 %

@Temperature 120 °C
 1.6 %

@Temperature 248 °F
1.8 %

@Temperature 150 °C
 1.8 %

@Temperature 302 °F
Tensile Modulus 11.0 GPa

@Temperature 150 °C
 1600 ksi

@Temperature 302 °F
15.0 GPa

@Temperature 120 °C
 2180 ksi

@Temperature 248 °F
21.0 GPa

@Temperature 90.0 °C
 3050 ksi

@Temperature 194 °F
23.5 GPa

@Temperature 60.0 °C
 3410 ksi

@Temperature 140 °F
25.0 GPa

@Temperature 23.0 °C
 3630 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 0.450 J/cm²
2.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Electrical Properties Metric English Comments
Volume Resistivity 6000 ohm-cm
6000 ohm-cm
Surface Resistance 300 ohm
300 ohm
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa