Alcoa Excalibar® 6013-T8 Aluminum, 1.9-3.8 cm diameter

Category	Metal , Nonferrous Metal , Aluminum Alloy , 6000 Series Aluminum Alloy
Manufacturer	Alcoa
Trade Name	Excalibar®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Alcoa Excalibar® 6013-T8 Aluminum, 1.9-3.8 cm diameter.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Weldability = A; Stress Corrosion Cracking Resistance = A; General Corrosion Resistance = B (A = best; E = worst). General 6013 characteristics and uses: High strength and good corrosion resistance. Easily joined by all welding and brazing methods. Excellent compressive properties. Good applied coating acceptance and good machinability.Uses: ABS Braking systems, hydraulic applications, valves, machine parts, roller blade parts, munitions.Data supplied by the manufacturer, Alcoa.

Physical Properties	Metric	English	Comments
Density	2.71 g/cc	0.0979 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	130	130	500 kg load/10 mm ball
Hardness, Knoop	163	163	Estimated from Brinell
Hardness, Rockwell A	49.5	49.5	Estimated from Brinell
Hardness, Rockwell B	80	80	Estimated from Brinell
Hardness, Vickers	149	149	Estimated from Brinell
Tensile Strength, Ultimate	>= 400 MPa	>= 58000 psi
Tensile Strength, Yield	>= 386 MPa	>= 56000 psi
Elongation at Break	8.0 %	8.0 %	in 5 cm.
Modulus of Elasticity	69.6 GPa	10100 ksi
Machinability	70 %	70 %	0-100 Scale (A=90; B=70; C=50; D=30; E=10)
Shear Strength	239 MPa	34700 psi	Calculated

Thermal Properties	Metric	English	Comments
CTE, linear	23.4 µm/m-°C @Temperature 20.0 - 100 °C	13.0 µin/in-°F @Temperature 68.0 - 212 °F	average
Thermal Conductivity	164 W/m-K	1140 BTU-in/hr-ft²-°F

Component Elements Properties	Metric	English
Aluminum, Al	97 %	97 %
Chromium, Cr	<= 0.10 %	<= 0.10 %
Copper, Cu	0.60 - 1.1 %	0.60 - 1.1 %
Iron, Fe	<= 0.50 %	<= 0.50 %
Magnesium, Mg	0.80 - 1.2 %	0.80 - 1.2 %
Manganese, Mn	0.20 - 0.80 %	0.20 - 0.80 %
Silicon, Si	0.60 - 1.0 %	0.60 - 1.0 %
Titanium, Ti	<= 0.10 %	<= 0.10 %
Zinc, Zn	<= 0.25 %	<= 0.25 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000450 ohm-cm	0.00000450 ohm-cm