LATI Kelon® B H CETG/300 PA 6, Glass/Mineral Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer LATI
Trade Name Kelon® B
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® B H CETG/300 PA 6, Glass/Mineral Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0055 cm/cm
0.0035 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0070 cm/cm
0.0045 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 150 °C
 3630 psi

@Temperature 302 °F
30.0 MPa

@Temperature 120 °C
 4350 psi

@Temperature 248 °F
35.0 MPa

@Temperature 90.0 °C
 5080 psi

@Temperature 194 °F
60.0 MPa

@Temperature 60.0 °C
 8700 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.2 %

@Temperature 60.0 °C
 3.2 %

@Temperature 140 °F
7.0 %

@Temperature 90.0 °C
 7.0 %

@Temperature 194 °F
15 %

@Temperature 120 °C
 15 %

@Temperature 248 °F
25 %

@Temperature 150 °C
 25 %

@Temperature 302 °F
Tensile Modulus 1.70 GPa

@Temperature 150 °C
 247 ksi

@Temperature 302 °F
2.20 GPa

@Temperature 120 °C
 319 ksi

@Temperature 248 °F
3.00 GPa

@Temperature 90.0 °C
 435 ksi

@Temperature 194 °F
3.60 GPa

@Temperature 60.0 °C
 522 ksi

@Temperature 140 °F
8.60 GPa

@Temperature 23.0 °C
 1250 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 240 - 290 °C
464 - 554 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa