Kuraray Vectran® HT 1500/300 LCP Fiber
| Category | Other Engineering Material , Composite Fibers , Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) |
| Manufacturer | Kuraray Company |
| Trade Name | Vectran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Vectran® HT 1500/300 LCP Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
 is a high-performance multifilament yarn spun from liquid crystal polymer (LCP).  fiber exhibits exceptional strength and rigidity. Pound for pound  fiber is five times stronger than steel and ten times stronger than aluminum.  features:High strength and modulusExcellent creep resistanceHigh abrasion resistanceExcellent flex/fold characteristicsMinimal moisture absorptionHydrolytically stableResistance to organic solventsStable to acids (
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 65% RH |
| Loss On Ignition | 28 % | 28 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 3200 MPa | 464000 psi | |
| Elongation at Break | 3.3 - 3.7 % | 3.3 - 3.7 % | |
| Tensile Modulus | 75.0 GPa | 10900 ksi | Initial Modulus |
| Tenacity | 2.03 - 2.38 N/tex | 23.0 - 27.0 g/denier |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | -11.6 µm/m-°C @Temperature 100 - 200 °C |
-6.44 µin/in-°F @Temperature 212 - 392 °F |
Longitudinal Fiber |
| -4.80 µm/m-°C @Temperature -150 - 100 °C |
-2.67 µin/in-°F @Temperature -238 - 212 °F |
Longitudinal Fiber | |
| Specific Heat Capacity | 1.10 J/g-°C @Temperature 23.0 °C |
0.263 BTU/lb-°F @Temperature 73.4 °F |
|
| 1.42 J/g-°C @Temperature 100 °C |
0.339 BTU/lb-°F @Temperature 212 °F |
||
| Thermal Conductivity | 1.50 W/m-K @Temperature 23.0 °C |
10.4 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
|
| 2.00 W/m-K @Temperature 100 °C |
13.9 BTU-in/hr-ft²-°F @Temperature 212 °F |
||
| Decomposition Temperature | >= 400 °C | >= 752 °F | charring begins |
| >= 450 °C | >= 842 °F | 20% weight loss; TGA | |
| Shrinkage | <= 0.20 % @Temperature 180 °C, Time 1800 sec |
<= 0.20 % @Temperature 356 °F, Time 0.500 hour |
Hot Air |
| <= 0.20 % @Temperature 100 °C, Time 1800 sec |
<= 0.20 % @Temperature 212 °F, Time 0.500 hour |
Boiling Water |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | <= 3 @Frequency 1e+10 Hz |
<= 3 @Frequency 1e+10 Hz |
Users viewing this material also viewed the following:
- MV Labs FE700 Fe(NO3)3·9H2O Iron(III) nitrate nonahydrate
- Polykemi AB POLYshine PBT D223 GF20 FR PBT, Glass-Fiber Reinforced, Flame Retardant
- Overview of materials for Nylon 612, Carbon Fiber Filler
- Lehmann & Voss LUVOCOM® 80/CF/12/TF/10/BK Polyacetal-copolymer, with carbon fiber and PTFE
- H.C. Starck Grade A Zirconium Diboride, ZrB2
- Struktol V-HCS Co-Stabilizing Processing Additive
- Zircar Ceramics HR-3A Dense Aluminum Oxide Support Rod
- Covestro Apec® 2097 Polycarbonate
- DSM Somos® WaterClear® Ultra 10122 Optically Clear, Colorless, Rigid, Stereolithography Resin
- ACC MM911 Condensation Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved