Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Abrasion Resistance HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It delivers low friction.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | |
| Water Absorption | 1.4 % | 1.4 % | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | |
| Melt Flow | 46 g/10 min @Load 2.16 kg, Temperature 320 °C |
46 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 5.50 cm @Load 750 kg, Temperature 320 °C |
2.17 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 47.0 MPa | 6820 psi | Weld; ASTM D638 |
| 165 MPa | 23900 psi | ASTM D638 | |
| Elongation at Yield | 0.70 % | 0.70 % | Weld; ASTM D638 |
| 4.0 % | 4.0 % | ASTM D638 | |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1.00e+10 Hz |
3.3 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.0090 @Frequency 1.00e+10 Hz |
0.0090 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM UL746A |
Users viewing this material also viewed the following:
- Omya HYDROCARB® PG-3 Calcium Carbonate
- Network Polymers NPP 25-1011B
- Kazanorgsintez PC-007 Polycarbonate
- Latrobe Lescalloy® HP 9-4-30 VAC-ARC ; 5.75 in RCS Billet Size High Strength Alloy Steel
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 20 lb
- Sibur NGP 40-32 Polyvinyl Chloride (PVC)
- Solvay IGEPAL® OD 410 Surfactant
- A. Schulman POLYFORT™ PP 2175HU Toyota High Flow Copolymer Polypropylene
- A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
- DSM Stanyl® 46HF4130 Nylon 46-30% Glass Reinforced (European and Asian Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved