BASF Elastollan 1185 A M TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyether Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan 1185 A M TPUR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Thermoplastic Polyether Polyurethane Elastomers with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms.Typical Applications: Cable sheathing, plugs and terminations, spiral tubing, films, ski boot shells, ear tags, technical moldings, e.g. mining screens, railway pads and seals.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.11 g/cc	0.0401 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	88	88	ISO 868
Hardness, Shore D	39	39	ISO 686
Tensile Strength	30.0 MPa	4350 psi	after storage in water at 80°C for 42 days; ISO 37
	45.0 MPa	6530 psi	ISO 37
	3.50 MPa @Strain 20.0 %	508 psi @Strain 20.0 %	ISO 37
	7.00 MPa @Strain 100 %	1020 psi @Strain 100 %	ISO 37
	12.0 MPa @Strain 300 %	1740 psi @Strain 300 %	ISO 37
Elongation at Break	600 %	600 %	ISO 37
	650 %	650 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DIN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	60.0 kN/m	342 pli	DIN ISO 34-1/Bb
Abrasion	60	60	[mm<sup>3</sup>; ISO 4649
Compression Set	35 % @Temperature 23.0 °C	35 % @Temperature 73.4 °F	ISO 815
	45 % @Temperature 70.0 °C	45 % @Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 220 °C	320 - 428 °F	Extrusion
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Extrusion