Kostat ICP-STAT ICD-1003 PS Sheet

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Extrusion Grade
Manufacturer Kostat
Trade Name ICP-STAT
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kostat ICP-STAT ICD-1003 PS Sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KOSTATs ICP-STAT is a thermoplastic sheet coated with an inherently conductive polymer (ICP). ICP-STAT has distinctive advantages in ESD and cleanliness performances compared to other materials based on Hygroscopic Antistats and Conductive Fillers. This product exhibits superior transparency and clarity.Special Features:Superior Permanent Static DissipationHumidity InsensitivityExcellent Wear resistanceLow Particle GenerationSuperior Transparency and ClarityLow Ionic ContaminationExcellent Chemical Resistance with Environmentally Friendly MaterialsApplications:Semiconductors PackagingLCD Components PackagingHDD Components PackagingElectrical & Electronics PackagingMedical Devices PackagingClean Room Accessories
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ASTM D638
Flexural Strength 77.9 MPa
11300 psi
ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 67.8 °C
154 °F
ASTM D648
Optical Properties Metric English Comments
Transmission, Visible >= 85 %
>= 85 %
ASTM D1003
Electrical Properties Metric English Comments
Surface Resistivity per Square 1e+05 - 1.00e+6 ohm
1e+05 - 1.00e+6 ohm
ASTM D257
1.00e+6 ohm
1.00e+6 ohm
after 100% elongation; ASTM D257
1.00e+7 ohm
1.00e+7 ohm
after 200% elongation; ASTM D257
1.00e+9 ohm
1.00e+9 ohm
after 250% elongation; ASTM D257