Kostat E-3007J Conductive PS Compound
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | Kostat |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kostat E-3007J Conductive PS Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOSTAT E-3007J is a conductive thermoplastic compound based on impact modified polystyrene and a special conductive carbon black.KOSTAT E-3007J is not dependant on atmospheric conditions.Special FeaturesThis product exhibits high conductivity, easy processing, smooth sheet surface, and tight dimensional tolerances after forming. This makes KOSTAT E3007J suitable for thermoforming various packaging products.Applications:KOSTAT E-3007J is recommended for electronics packaging such as ESD sheets, Carrier Tapes, Formed tray sheets, and other extruded products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 30.0 MPa | 4350 psi | ASTM D790 |
| Flexural Modulus | 19.6 GPa | 2840 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | Kostat Rv |
| Surface Resistivity per Square | 1e+05 | 1e+05 | Kostat Rs |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 °C | 374 °F | C1 |
| Middle Barrel Temperature | 200 °C | 392 °F | C3 |
| Front Barrel Temperature | 210 °C | 410 °F | C5 |
| Die Temperature | 87.8 °C | 190 °F | D3 |
| 93.3 °C | 200 °F | D5 | |
| 93.3 °C | 200 °F | D1 | |
| Roll Temperature | 60.0 °C | 140 °F | 3rd |
| 80.0 °C | 176 °F | 2nd | |
| 90.0 °C | 194 °F | 1st |
Users viewing this material also viewed the following:
- PolyMirae Moplen HP557G Stretch Grade Polypropylene
- Lord Adhesives 5000 Fast Setting, High Elasticity, Low Viscosity Ethyl Cyanoacrylate Adhesive
- Latrobe LSSâ„¢ A7 Mod. Wear-Resistant Tool Steel (ASTM A7 Mod.)
- Menzolit Menzolit® BMC 2910 Unsaturated Polyester UP
- Styron Pulse® 959 ABS + Polycarbonate, 10% Glass Reinforced
- ExxonMobil Mobil Vactra 4
- Eurotec® Tecotek® PC43 GR20 BK002 PC, 20% glass fiber reinforced, black
- Arlon R39118R037L 0.037" (0.940 mm) Cured Silicone Rubber with Fiberglass Substrate
- DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved