Kolon KOPET® KP133G15BL G/F Reinforced Polyester Compound Resin (PET)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced |
| Manufacturer | Kolon |
| Trade Name | KOPET® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPET® KP133G15BL G/F Reinforced Polyester Compound Resin (PET).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Dimensionally stable, high elastic, high flowApplications: Ink CartridgeInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength | 98.0 MPa | 14200 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 5.394 GPa | 782.3 ksi | ASTM D790 |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Arc Resistance | 119 sec | 119 sec | ASTM D495 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JJX20A Polyvinyl Chloride, Flexible (PVC, Flexible)
- Unipetrol PP MONSTEN® MA 745 Polypropylene Impact Copolymer
- EMS-Grivory Grivory® 2S 25 W 20 X nat PA610-I
- ExxonMobil LD 129.24 Cast Overwrap Film Resin
- Aremco Lamp-Coat™ LC4010-BT High Temperature Coating, Silicone
- Arkema Group LOTRYL® 14 MGC 02 Copolymer Ethylene - Methyl Acrylate
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 10% Cold Rolled (UNS S30200)
- Teknor Apex Sinpolene MBW0442 Low Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved