- Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66
Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333MT30BL Mineral Reinforced Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MF reinforcedApplications Cam shaftsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength | 74.0 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 118 MPa | 17100 psi | ASTM D790 |
| Flexural Modulus | 4.119 GPa | 597.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 | 3.4 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Arc Resistance | 133 sec | 133 sec | ASTM D495 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-509OR-JM PVC Compound
- Lanxess Durethan® BC 700 HTS DUSXBL 900116 Nylon 6, Impact Modified
- Samyang Triloy® 130 PC/PBT alloy
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- A. Schulman POLYBATCH™ 10178Z Amber Concentrate Based in LDPE
- CLAL-MSX ARCAP Anticorrosion AP4 H13 3/4 hard, Drawn Copper Alloy
- BASF Capron® 8259 Impact Modified Nylon 6 (Dry) (discontinued **)
- Ashley Polymers Ashlene® P1053R Polycarbonate
Copyright © lookpolymers.com All Rights Reserved