- Kobe Steel KS70 Commercially Pure Titanium, ASTM Gr. 3, Annealed
Kobe Steel KS70 Commercially Pure Titanium, ASTM Gr. 3, Annealed
| Category | Metal , Nonferrous Metal , Titanium Alloy |
| Manufacturer | Kobe Steel |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kobe Steel KS70 Commercially Pure Titanium, ASTM Gr. 3, Annealed.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nominal Composition: Ti-Fe-OApplications: Tube sheets.Features: Relatively high strength, excellent corrosion resistance.Information provided by Kobe Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.50 g/cc | 0.163 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 450 MPa | >= 65300 psi | |
| Tensile Strength, Yield | 380 - 550 MPa @Strain 0.200 % |
55100 - 79800 psi @Strain 0.200 % |
|
| Elongation at Break | >= 18 % | >= 18 % | |
| Reduction of Area | >= 30 % | >= 30 % | |
| Bend Radius, Minimum | 2.0 t | 2.0 t | t ≤ 1.8 mm |
| 2.5 t | 2.5 t | 1.8 < t ≤ 4.75 mm |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.080 % | <= 0.080 % | |
| Hydrogen, H | <= 0.015 % | <= 0.015 % | |
| Iron, Fe | <= 0.30 % | <= 0.30 % | |
| Nitrogen, N | <= 0.050 % | <= 0.050 % | |
| Oxygen, O | <= 0.35 % | <= 0.35 % | |
| Titanium, Ti | >= 99.205 % | >= 99.205 % | As Remainder |
Users viewing this material also viewed the following:
- PolyOne Stat-Tech™ PC-CB2/000 CR Polycarbonate (PC)
- Kingfa FRHIPS-930 Flame Retardant Polystyrene
- Solvay MACKCONDITIONERâ„¢ CBS Surfactant
- Washington Penn Homopolymer Polypropylene 30% Talc Filled
- Polyram RamLloy PN300G4 PPE/PS Alloy, 20% Glass Fiber
- Arlon 41580R015 0.015" Uncured, Unsupported Silicone Rubber on Release Carrier
- Solvay RHODAFAC® RA-600 E Surfactant
Copyright © lookpolymers.com All Rights Reserved