KYDEX® 6185 Thermoplastic Sheet

Category Polymer , Thermoplastic
Manufacturer KYDEX LLC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF KYDEX® 6185 Thermoplastic Sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High temperature aircraft gradeApplications: Aircraft interior components examples include: air ducts, window reveals, instrument panels, toilet shrouds, armrestsFeatures: Kydex 6185 is a proprietary thermoplastic sheet with improved heat distortion temperature (HDT) for higher in-service temperatures while providing excellent extensibility, good impact resistance, and excellent solvent resistance. It meets FAR 25.853(a) for use in aircraft interior parts. Maximum recommended service temperature is approx. 82-90°C depending on thermoforming technique and application. Kydex 6185 sheet is designed primarily for use in small aircraft interiors particularly the interior of helicopters which often experience temperature in excess of 82°C, but also is appropriate for other applications where high in-service temperatures may occur.Fabrication: Excellent forming properties result in uniform wall thicknesses and crisp detail, plus easy machining and fabricating using conventional methods, further expanding finished part possibilities.Data provided by the Kleerdex Company.
Physical Properties Metric English Comments
Density 1.33 - 1.37 g/cc
0.0480 - 0.0495 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 104
104
ASTM D785
Tensile Strength, Ultimate 44.0 MPa
6380 psi
ASTM D638
Elongation at Break 100 %
100 %
Modulus of Elasticity 2.241 GPa
325.0 ksi
Flexural Yield Strength 66.0 MPa
9570 psi
ASTM D790
Izod Impact, Notched 2.67 J/cm

@Temperature 23.0 °C
5.00 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
annealed; ASTM D648
Flammability, UL94 V-0
V-0
Processing Properties Metric English Comments
Processing Temperature 163 - 200 °C
325 - 392 °F
Forming Temperature