Honeywell Capran® Oxyshield™ OXTR (Retortable Grade, 0.6 mil) Monoaxially Oriented Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ OXTR (Retortable Grade, 0.6 mil) Monoaxially Oriented Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Oxyshield™ Oriented Ultra Barrier Retortable Grade is a monoaxially oriented, co-extruded nylon 6-based clear film having excellent gas barrier through a broad range of relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Water Vapor Transmission | 301 g/m²/day | 19.4 g/100 in²/day | 100°F (37.8°C) / 97%RH; ASTM F1249 |
| Oxygen Transmission Rate | 1.38 cc/m²/day | 0.0889 cc/100 in²/day | 73°F (23°F) / 65%RH; ASTM D3985 |
| 2.05 cc/m²/day | 0.132 cc/100 in²/day | 73°F (23°C) / 0%RH; ASTM D3985 | |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 78 % | 78 % | ASTM D882 |
| Film Elongation at Break, TD | 410 % | 410 % | ASTM D882 |
| Coefficient of Friction | 0.25 | 0.25 | film to stainless steel; ASTM D1894 |
| 0.70 | 0.70 | film to film; ASTM D1894 | |
| Tear Strength Test | 636 | 636 | graves tear MD, grams/mil; ASTM D1004 |
| 1139 | 1139 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 269 MPa | 39000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 103 MPa | 15000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | <= 93.0 °C | <= 199 °F | continuous use temperature |
| <= 176 °C | <= 349 °F | short time use temperature | |
| Shrinkage, MD | 12.6 % | 12.6 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | 2.1 % | 2.1 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- MV Labs MN820 MnO2 Manganese(IV) oxide
- Nilit FRIANYL B63 FK 1020 Nylon 6 for injection molding, 10% glass fiber and 20% glass ball reinforced
- Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride (discontinued **)
- Solvay Specialty Polymers Galden® HS260 PFPE VPS Fluid
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 50 PHR N990 (MT) Filler
- Westlake Plastics Radel® R 5500 Polyphenylsulfone For Medical Applications
- A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer
- DuPont Teijin Films Melinex® ST506 Polyester Film, 700 Gauge
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR Laminar Filler
- Hexcel® HexPly® 920KX-285-52% 125°C Curing Epoxy Matrix
Copyright © lookpolymers.com All Rights Reserved