Iran Petrochemical (PCC) EX 6HT HM 9455 HT High Density Polyethylene

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Iran Petrochemical Commercial Co. (PCC)
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Iran Petrochemical (PCC) EX 6HT HM 9455 HT High Density Polyethylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EX 6HT is a high density polyethylene with 1-Butene as co monomer. It has good toughness, low gel level, good tear strength, high tenacity.Applications: film extrusion, blending partner, refuse bags, carrier bags, heavy duty packing.Information provided by Iran Petrochemical Commercial Co.

Physical Properties	Metric	English	Comments
Density	0.944 g/cc	0.0341 lb/inÂ³	ISO 1183
Melt Flow	0.18 g/10 min @Load 5.00 kg, Temperature 190 Â°C	0.18 g/10 min @Load 11.0 lb, Temperature 374 Â°F	ISO 1133
	5.4 g/10 min @Load 21.6 kg, Temperature 190 Â°C	5.4 g/10 min @Load 47.6 lb, Temperature 374 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	58	58	ISO 868
Tensile Stress	36.0 MPa	5220 psi	at Break; ISO 527
Tensile Strength, Yield	21.0 MPa	3050 psi	ISO 527
Film Elongation at Break, MD	<= 450 %	<= 450 %	ISO 527
Film Elongation at Break, TD	<= 500 %	<= 500 %	ISO 527
Elmendorf Tear Strength MD	20.4 g	20.4 g	ISO 6383-2
Elmendorf Tear Strength TD	40.8 g	40.8 g	ISO 6383-2
Dart Drop Test	240 g	0.529 lb	ASTM D1709
Film Tensile Strength at Break, MD	<= 45.0 MPa	<= 6530 psi	ISO 527
Film Tensile Strength at Break, TD	<= 40.0 MPa	<= 5800 psi	ISO 527

Thermal Properties	Metric	English	Comments
Softening Point	73.0 Â°C	163 Â°F	ISO 306
Brittleness Temperature	>= -80.0 Â°C	>= -112 Â°F	ASTM D746-72

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 230 Â°C	392 - 446 Â°F