Iran Petrochemical (PCC) BL2 HF 4750 High Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | Iran Petrochemical Commercial Co. (PCC) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Iran Petrochemical (PCC) BL2 HF 4750 High Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BL2 is a high density polyethylene with 1-Butene as co monomer. It is high impact strength and slightly, lower stiffness than BL3, outstanding resistance to stress cracking, even in contact with surfactants.Applications: small blow molding, bottles, containers (up to 5 L), packing of pharmaceuticals & surfactants.Information provided by Iran Petrochemical Commercial Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.944 g/cc | 0.0341 lb/in³ | ISO 1183 |
| Environmental Stress Crack Resistance | 10 hour @Pressure 3.50 MPa |
10 hour @Pressure 508 psi |
ISO CD 16770 |
| Melt Flow | 1.1 g/10 min @Load 5.00 kg, Temperature 190 °C |
1.1 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| 23 g/10 min @Load 21.6 kg, Temperature 190 °C |
23 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ISO 868 |
| Tensile Stress | 32.0 MPa | 4640 psi | at Break; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Break | >= 600 % | >= 600 % | ISO 527 |
| Elongation at Yield | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Softening Point | 70.0 °C | 158 °F | ISO 306 |
| Brittleness Temperature | >= -80.0 °C | >= -112 °F | ASTM D746-72 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 280 °C | 392 - 536 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexural Creep Modulus (MPa) | 1050 | 4 point, 1 min; DIN 19537-2 |
| Swell Ratio, % | 120 |
Users viewing this material also viewed the following:
- DuPont Bynel® 1E554 Modified EVA Adhesive Resin (discontinued **)
- DuPont Performance Polymers Zytel® 444AHS BK152 Nylon 66 (Unverified Data**)
- Huntsman Araldite GT 9545 Bisphenol A Epoxy Solid Resin
- Sharadaa Ceramics HH 42D Normal Medium and High Heat and Super Duty Brick
- Techmer ES HiFill® PA6 1030
- Hexcel® HexTow™ 1925/IM Chopped Fiber
- Hippe UP GM 205 Woven Glass Mat Reinforced Polyester (unsaturated) Resin - Sheet
- AK Steel PH 15-7 Mo® Precipitation Hardening Stainless Steel, Condition TH 1050
- Polyram Polytron P30B01 Homopolymer Polypropylene, Chemically Coupled 30% LGF
- Huntsman Araldite GZ 488 V-32 US Bisphenol A Epoxy Solution
Copyright © lookpolymers.com All Rights Reserved