LyondellBasell Astryn BA65H Polypropylene Copolymer, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | LyondellBasell |
| Trade Name | Astryn |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Astryn BA65H Polypropylene Copolymer, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: high melt flow, medium modulus, flame retardant polypropylene copolymer, good electrical properties, good aesthetics and colorability, good processabilityApplications: furniture, small appliances, housewaresDescription: Astryn BA65H conventional melt flow, UL 94 V-2 flame tretardant polypropylene copolymer has an excellent cobination of properties and processability. It was designed for application which require flame and heat resistance, along with good electrical properties, high impact strenght and good surface quality.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792B |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Tool, Montell |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | ASTM D785 |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 45 % | 45 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | 1% secant at 0.05 in/min; ASTM D790A |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256A |
| Gardner Impact | 27.0 J | 19.9 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ASTM D648 |
| UL RTI, Mechanical with Impact | 115 °C @Thickness 3.00 mm |
239 °F @Thickness 0.118 in |
ASTM UL94 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|
| Oxygen Index | 28 % | 28 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 8.90e+16 ohm-cm | 8.90e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 27.1 kV/mm | 688 kV/in | ASTM D149 |
| Arc Resistance | 133 sec | 133 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Hogen Durakut H15W 68 Tungsten/32 Copper PM Metal Composite
- M. Holland Company CP310 Polypropylene Impact Copolymer
- MarkeTech Repton 838 Zirconia + 3 mol% Yttria (YSZ)
- Lushan RF1000 Adhesive Resin for Aluminum Plastic Composite Pipe
- SABIC Innovative Plastics ULTEM PW1000 PEI (Europe-Africa-Middle East)
- Solvay Specialty Polymers Tecnoflon® FOR 537 Fluoroelastomer
- A. Schulman PP 1259 Polypropylene Medium Impact Polypropylene
- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
- 3M Pronto™ CA-7 Instant Adhesive
- Fainplast Compounds PMP 57 Flexible PVC, Extrusion Modified with PU
Copyright © lookpolymers.com All Rights Reserved