Inno-Comp INNOPOL® CS 2-9000 MA N Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-9000 MA N Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-9000 MA N is a high melt flow copolymer with antistatic additive.INNOPOL® CS 2-9000 MA N is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc @Temperature 23.0 °C |
0.0325 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | ISO 294 |
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 230 °C |
45 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 26 % | 26 % | ISO 527-1,-2 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.45 GPa | 210 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 1.58 GPa | 229 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 86.0 J/cm² @Temperature -30.0 °C |
409 ft-lb/in² @Temperature -22.0 °F |
PB; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 163 °C | 325 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | ISO 75-1,-2 |
| Vicat Softening Point | 81.0 °C | 178 °F | B120; ISO 306 |
| 147 °C | 297 °F | A120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Natural |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ OM 6160-9 Thermoplastic Elastomer (TPE)
- Michelman® Hydrosize® U2-01 Nonionic polyurethane emulsion
- Teknor Apex Sarlink® 3440 Thermoplastic Elastomer
- Lubrizol Estane® X-585A-31 Thermoplastic Polyurethane
- Borealis Daploy™ WF420HMS High Melt Strength Polypropylene for Extrusion Coating
- CeramTec Alunit® HS Aluminum Nitride
- Zotefoams Plastazote® LD32CN Conductive Low Density Polyethylene Foam
- Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate
Copyright © lookpolymers.com All Rights Reserved