Inno-Comp INNOPOL® CS 1-2140 BLH 40% Talc-Filled Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 1-2140 BLH 40% Talc-Filled Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 1-2140 BLH is recommended especially for producing products, where high stiffness, low shrinkage, long term heat stability and excellent processability are required.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc @Temperature 23.0 °C |
0.0441 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 37 % @Temperature 600 °C |
37 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 6.5 % | 6.5 % | ISO 527-1,-2 |
| Elongation at Yield | 3.2 % | 3.2 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 1.10 J/cm² @Temperature -30.0 °C |
5.24 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 2.50 J/cm² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.220 J/cm² @Temperature 23.0 °C |
1.05 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C | 268 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | ISO 75-1,-2 |
| Vicat Softening Point | 90.0 °C | 194 °F | B120; ISO 306 |
| 153 °C | 307 °F | A120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Resin Technology Group Fusion 543 Ultra Performance Fusion Cyanoacrylate
- Industeel Superplast® 350 Mold Steel
- Lubriplate AC-1 Petroleum-Based Air Compressor Fluid
- Isoflon PC Polycarbonate
- Fiberfil® PP-60/CC/20 Polypropylene Homopolymer, 20% Calcium Carbonate
- Solvay Chemicals Ixper® 35M Magnesium Peroxide
- SABIC Innovative Plastics LNP THERMOCOMP RX10405H PA 66
- Eagle Brass 425 Tin Brass 2%, 3/4 Hard
- Axiall EX1188B Wire & Cable Flexible PVC
Copyright © lookpolymers.com All Rights Reserved