Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
Manufacturer | Ineos Olefins & Polymers USA |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Ineos TUB 121 HDPE.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.9485 g/cc | 0.03427 lb/in³ | Natural; ASTM D4883 |
0.959 g/cc | 0.0346 lb/in³ | Black; ASTM D4883 | |
Environmental Stress Crack Resistance | >= 5000 hour | >= 5000 hour | Condition C; ASTM D1693 |
Carbon Black Loading | 2.3 % | 2.3 % | ASTM D1603 |
Melt Flow | 8.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
8.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
PENT | >= 10000 hour | >= 10000 hour | Notched Tensile; ASTM F1473 |
Hardness, Shore D | 66 | 66 | ASTM D2240 |
Tensile Strength at Break | 37.9 MPa | 5500 psi | 2 in/min; ASTM D638 |
Tensile Strength, Yield | 24.99 MPa | 3625 psi | 2 in/min; ASTM D638 |
Elongation at Break | >= 600 % | >= 600 % | 2 in/min; ASTM D638 |
Flexural Modulus | 1.03 GPa | 150 ksi | 2% Secant-Method 1; ASTM D790 |
Izod Impact, Notched | 4.81 J/cm | 9.00 ft-lb/in | ASTM D256 |
Hydrostatic Design Basis | 6.89 MPa | 1000 psi | at 60°C; ASTM D2837 |
11.0 MPa @Temperature 23.0 °C |
1600 psi @Temperature 73.4 °F |
ASTM D2837 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
Brittleness Temperature | <= -118 °C | <= -180 °F | ASTM D746 |
Decomposition Temperature | >= 220 °C | >= 428 °F | Thermal Stability; ASTM D2513/D3350 |
Descriptive Properties | Value | Comments |
---|---|---|
Cell Classification | 445574C | |
Process | Pipe Extrusion |