Arkema Group LOTADER® 6200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category Polymer , Thermoplastic , EMAAA Terpolymer
Manufacturer Arkema
Trade Name LOTADER®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group LOTADER® 6200 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LOTADER 6200 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. Due to its properties (reactivity, fluidity), LOTADER 6200 is an additive of choice for hot melt adhesives formulation. It is also use as a coupling agent in mineral filled compounds.Information provided by Arkema Group
Physical Properties Metric English Comments
Density 0.940 g/cc

@Temperature 23.0 °C
0.0340 lb/in³

@Temperature 73.4 °F
ISO 1183
Melt Index of Compound 40 g/10 min

@Load 2.16 kg,
Temperature 190 °C
40 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 36
36
ASTM D2240
Tensile Strength at Break 10.0 MPa
1450 psi
ASTM D638
Elongation at Break 600 %
600 %
ASTM D638
Flexural Modulus 0.0950 GPa
13.8 ksi
ASTM D638
Thermal Properties Metric English Comments
Melting Point 102 °C
216 °F
DSC
Vicat Softening Point 70.0 °C

@Load 0.999 kg
158 °F

@Load 2.20 lb
ASTM D1525
Ring & Ball Softening Point 119 °C
246 °F
ASTM E28
Chemical Properties Metric English Comments
Acid Value 17
17
mg KOH/g; Titration
Processing Properties Metric English Comments
Processing Temperature <= 300 °C
<= 572 °F
Descriptive Properties Value Comments
Ethyl Acrylate Content (%) 6.5
IRTF (internal)
Maleic Anhydride Content (%) 2.8
IRTF (internal)