ExxonMobil HD 6704.18 Injection Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil HD 6704.18 Injection Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HD 6704 is a narrow molecular weight hexane copolymer designed for outstanding balance of ESCR, Toughness and Stiffness properties. This resin is ideally suited for heavy-duty applications that require robust performance in conditions ranging from ambient to sub-zero temperatures.Availability: Latin America, North America and South America Additive: Antioxidant: YesApplications: Industrial Caps & ClosuresIndustrial PailsPackaging Drum LidsRecreational Vehicle - Components Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D4883
Environmental Stress Crack Resistance 6.0 hour
6.0 hour
Cond. B, 10%; ASTM D1693
Melt Flow 4.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
4.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 26.20 MPa
3800 psi
ASTM D638
Elongation at Break 1200 %
1200 %
ASTM D638
Flexural Modulus 1.17 GPa
170 ksi
2% Secant; ASTM D790
Flexural Modulus, 1% Secant 1310 MPa
190000 psi
ASTM D790
Izod Impact, Notched 0.587 J/cm

@Temperature -40.0 °C
1.10 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 132 °C
270 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 66.6 °C
152 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 39.0 °C
102 °F
ASTM D648
Descriptive Properties Value Comments
Features Standard Processing Antioxidants Stabilizer
Form Pellet