Ineos ABS Lustran® Guardian™ 620 ABS, Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® Guardian™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® Guardian™ 620 ABS, Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® Guardian™ ABS 620 is a high modulus, HFC 134a and HCFC 22 resistant extrusion grade resin designed for refrigerator door and food liners. Lustran® ABS 620 offers good melt strength and deep draw formability for superior material distribution in large complex parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM-D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.7 MPa | 4600 psi | ASTM-D638 |
| Tensile Strength, Yield | 38.6 MPa | 5600 psi | ASTM-D638 |
| Elongation at Break | 45 % | 45 % | ASTM-D638 |
| Elongation at Yield | 0.62 % | 0.62 % | 50/50 CO/OA, Critical |
| Tensile Modulus | 2.62 GPa | 380 ksi | ASTM-D638 |
| Flexural Yield Strength | 70.3 MPa | 10200 psi | ASTM-D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.908 J/cm @Temperature -17.8 °C |
1.70 ft-lb/in @Temperature 0.000 °F |
1/8" x 1/2" bar; ASTM-D256 (Method A) |
| 2.72 J/cm @Temperature 22.8 °C |
5.10 ft-lb/in @Temperature 73.0 °F |
1/8" x 1/2" bar; ASTM-D256 (Method A) | |
| Impact Test | 13.6 J @Temperature -17.8 °C |
10.0 ft-lb @Temperature 0.000 °F |
Multiaxial Impact, Driven Dart; 1/2" dart, 1-1/2" ring; E-max; ASTM-D3763 |
| 14.9 J @Temperature -17.8 °C |
11.0 ft-lb @Temperature 0.000 °F |
Multiaxial Impact, Driven Dart; 1/2" dart, 1-1/2" ring; E-tot; ASTM-D3763 | |
| 33.9 J @Temperature 22.8 °C |
25.0 ft-lb @Temperature 73.0 °F |
Multiaxial Impact, Driven Dart; 1/2" dart, 1-1/2" ring; E-max; ASTM-D3763 | |
| 47.5 J @Temperature 22.8 °C |
35.0 ft-lb @Temperature 73.0 °F |
Multiaxial Impact, Driven Dart; 1/2" dart, 1-1/2" ring; E-tot; ASTM-D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.8 °C | 208 °F | ASTM-D648 |
| Flammability, UL94 | HB @Thickness 1.05 mm |
HB @Thickness 0.0413 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 98 % | 98 % | Angle 60°; Gardner |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Die Temperature | 210 - 250 °C | 410 - 482 °F | |
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | Extruder |
| Roll Temperature | 74.0 °C | 165 °F | Down Stack, Middle |
| 93.0 °C | 199 °F | Down Stack, Bottom | |
| 93.0 °C | 199 °F | Down Stack, Top | |
| Drying Temperature | 82.0 - 90.0 °C @Time 10800 - 14400 sec |
180 - 194 °F @Time 3.00 - 4.00 hour |
|
| Moisture Content | <= 0.030 % | <= 0.030 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pump Ratio | 1.5-2.0 | Extrusion |
| Screw Compression Ratio | 2.5-2.7 | Extrusion |
Users viewing this material also viewed the following:
- PSM Industries Pacific Sintered Metals High Carbon Copper Steel FCC-214-S Powdered Metal
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 59 Shore A (discontinued **)
- Schott S8807 Contrast Enhancement Filter
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-550 (FEF)
- EPICHEM Epiter PBT GF 30 Polybutylene Terephthalate, 30% Glass
- Colorite Polymers 6088 Non-Phthalate 88 Series Vinyl Compound
- Arlon 44560R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Plating Grade
- Eurostar Star L PA66 15Y D61 PA66, Carbon Filled, Injection Molded
Copyright © lookpolymers.com All Rights Reserved