- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Ineos ABS Lustran® ABS 241 ABS, Blending Grade
Ineos ABS Lustran® ABS 241 ABS, Blending Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 241 ABS, Blending Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 241 resin is a natural, stiffer-flow, virgin blending grade of ABS (acrylonitrile butadiene styrene). It is designed for use with other high-impact ABS resins for drain, waste, and vent (DWV) pipe and fittings. Lustran® ABS 241 resin in natural color (000000) meets or exceeds ASTM D 3965 1-1-2-2-2 cell class requirements. It is also listed under NSF Standard 14.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM-D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 290 °C |
15 g/10 min @Load 22.0 lb, Temperature 554 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ASTM-D638 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ASTM-D638 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.50 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM-D256 |
| 1.39 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.60 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C @Thickness 6.40 mm |
216 °F @Thickness 0.252 in |
ASTM-D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 243 °C | 450 - 469 °F | Injection Molding |
| 232 - 243 °C | 450 - 469 °F | Extrusion | |
| Mold Temperature | 43.0 - 66.0 °C | 109 - 151 °F | Injection Molding |
| Drying Temperature | 82.0 - 93.0 °C @Time 7200 sec |
180 - 199 °F @Time 2.00 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Moderately High to High, Injection Molding | |
| Injection Speed | Moderate to Fast | Injection Molding |
| Screw Compression Ratio | 2.4-2.8:1 | Extrusion |
| Screw Length-to-Diameter Ratio | 24-36:1 | Extrusion |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF60 - PP Homopolymer Polypropylene, 60% Long Glass Fiber Reinforced
- Omnia Plastica Omniamid PA 6 - Akulon 6 - at 50% RH
- Quadrant EPP TIVAR® Dryslide PE-UHMW + internal lubricant + other additives (ISO Data)
- Solvay Specialty Polymers Ixef® 3006/9019 Polyarylamide, 30% Carbon Fiber, at Equilibrium (65% RH) (discontin
- Iran Petrochemical (PCC) PC 5970 Polycarbonate
- Fujipoly Industries Sarcon® 85T Thin-Film TR
- Unifrax Fiberfrax® HSA-HP High Purity High-Index Fiber
- Polyram PlusTek RA314G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized
- DuPont Performance Polymers Delrin® 500AL NC010 Acetal (POM) (Unverified Data**)
- Carpenter Chrome Core® 18-FM Solenoid Quality Stainless Steel, Annealed
Copyright © lookpolymers.com All Rights Reserved