PolyOne Edgetek® PS-20GF/000 NATURAL Polybutylene Terephthalate (PBT)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer	PolyOne Corporation
Trade Name	Edgetek®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Edgetek® PS-20GF/000 NATURAL Polybutylene Terephthalate (PBT).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.45 g/cc	1.45 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm @Thickness 3.18 mm	0.0030 - 0.0050 in/in @Thickness 0.125 in	ASTM D955
Linear Mold Shrinkage, Transverse	0.013 - 0.015 cm/cm @Thickness 3.18 mm	0.013 - 0.015 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	96.5 MPa	14000 psi	5.1 mm/min; ASTM D638
Elongation at Break	3.0 - 5.0 %	3.0 - 5.0 %	ASTM D638
Tensile Modulus	6.76 GPa	980 ksi	5.1 mm/min; ASTM D638
Flexural Strength	165 MPa	23900 psi	1.3 mm/min; ASTM D790
Flexural Modulus	6.00 GPa	870 ksi	1.3 mm/min; ASTM D790
Izod Impact, Notched	0.590 J/cm	1.11 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	219 °C	426 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	182 °C	360 °F	Unannealed; ASTM D648

Descriptive Properties	Value	Comments
Agency Ratings	FDA Unspecified Rating
Features	Good Chemical Resistance
	High Heat Resistance
	Semi Crystalline
Filler / Reinforcement	Glass Fiber Reinforcement, 20% Filler by Weight
Forms	Pellets
Generic Material	PBT
Generic Name	Polybutylene Terephthalate (PBT)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Appliance Components
	Appliances
	Automotive Applications
	Consumer Applications
	Housings
	Industrial Applications
	Structural Parts

Users viewing this material also viewed the following: