Industeel SIRIUS S12 20% Cr - 1.8% Si Heat Resistant Steel
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | SIRIUS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel SIRIUS S12 20% Cr - 1.8% Si Heat Resistant Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLI SIRIUS S12 grade is an austenitic stainless steel containing 20% Cr, 1.8 % Si and 12% Ni. The low nickel content combined with high chromium and high silicon contents provide good resistance to high temperature oxidation, even in sulphur containing gases The structure stability of the grade is enhanced compared to other more alloyed heat resistant steels. The alloy is designed to resist in oxidizing atmospheres up to 1000°C (1832°F). In cyclic conditions, a maximum temperature of 950°C (1742°F) should be considered. The alloy performs much better than 304 H and 304 N grades.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.90 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 540 MPa | 78300 psi | Typical after Solution Annealing |
| Tensile Strength, Yield | 245 MPa @Strain 0.200 % |
35500 psi @Strain 0.200 % |
Typical after Solution Annealing |
| 265 MPa @Strain 1.00 % |
38400 psi @Strain 1.00 % |
Typical after Solution Annealing | |
| Elongation at Break | 40 % | 40 % | Typical |
| Creep Strength | 140 MPa @Temperature 600 °C, Time 3.60e+6 sec |
20300 psi @Temperature 1110 °F, Time 1000 hour |
|
| Modulus of Elasticity | 200 GPa | 29000 ksi | |
| Poissons Ratio | 0.333 | 0.333 | Calculated |
| Shear Modulus | 75.0 GPa @Temperature 20.0 °C |
10900 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 18.0 µm/m-°C @Temperature 20.0 - 400 °C |
10.0 µin/in-°F @Temperature 68.0 - 752 °F |
||
| 18.5 µm/m-°C @Temperature 20.0 - 600 °C |
10.3 µin/in-°F @Temperature 68.0 - 1110 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C @Temperature 20.0 °C |
0.120 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 15.0 W/m-K @Temperature 20.0 °C |
104 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 20 % | 20 % | |
| Iron, Fe | 66.1 - 66.2 % | 66.1 - 66.2 % | As remainder |
| Nickel, Ni | 12 % | 12 % | |
| Silicon, Si | 1.8 % | 1.8 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000900 ohm-cm @Temperature 20.0 °C |
0.0000900 ohm-cm @Temperature 68.0 °F |
Users viewing this material also viewed the following:
- MV Labs CR700 Cr(NO3)3·9H2O Chromium(III) nitrate nonahydrate
- Potters Industries A-Series Premium 5MM Soda-Lime Silica Technical Quality Solid Glass Spheres
- Solvay Specialty Polymers KetaSpire® KT-880 CF30 Polyetheretherketone (PEEK) (Unverified Data**)
- KB Alloys Tibor® 5% Ti - 0.1% B Titanium Boron Aluminum Alloy
- Momentive Performance Materials Siloprenâ„¢ LSR 3186/50 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Teknor Apex APEX® 280-NL Polyvinyl Chloride, Flexible
- Weartech International NOREM 02A Iron Hardfacing & Wear Resistant Alloy
- EMS-Grivory Grivory® HTV-3H1 nat PA6T/6I-GF30
- Ametek High Purity Nickel Strip 899A Hard
- SABIC Innovative Plastics NORYL FN170X PPE+PS
Copyright © lookpolymers.com All Rights Reserved