- Honeywell Capran® Emblem™ 1500 Clear Bi-Axially Oriented Nylon Film
Honeywell Capran® Emblem™ 1500 Clear Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 1500 Clear Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 1500 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock.Applications: bag-on-box packaging, packaging for processed meats, cheese, meat snacks, coffee bricks, coffee bags, and pet food, agricultural bags, stand-up shampoo pouches, book covers and metallized balloons.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 310 - 357 g/m²/day | 20.0 - 23.0 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 46.56 - 62.08 cc/m²/day | 2.998 - 3.998 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 15.2 microns | 0.600 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 60 - 110 % | 60 - 110 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 100 % | 60 - 100 % | ASTM D882 |
| Secant Modulus, MD | 2.41 - 3.52 GPa | 350 - 511 ksi | ASTM D882 |
| Secant Modulus, TD | 2.275 - 3.45 GPa | 330.0 - 500 ksi | ASTM D882 |
| Coefficient of Friction | 0.18 - 0.27 | 0.18 - 0.27 | film to stainless steel; ASTM D1894 |
| 0.59 - 0.60 | 0.59 - 0.60 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear, grams/mil (initial); ASTM D1004 |
| Elmendorf Tear Strength, MD | 0.5248 - 0.7217 g/micron | 13.33 - 18.33 g/mil | |
| Film Tensile Strength at Break, MD | 221 - 303 MPa | 32000 - 44000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 200 - 283 MPa | 29000 - 41000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.4 - 2.4 % | 1.4 - 2.4 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.3 % | <= 3.3 % | ASTM D1003 |
| Gloss | 160 - 175 % | 160 - 175 % | at 20° |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G90S White Perfluoroelastomer
- NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin
- Overview of materials for Polycarbonate, Carbon + Glass Fiber Reinforced
- Kleerdex Kydex® IM62 Acrylic/PVC injection Molding Compound (discontinued **)
- LATI Larton K/40 HM PPS, 40% Carbon Fiber Reinforced
- Heatbath/Park High Speed 75 High Speed Hardening Salt
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- A. Schulman SCHULAMID® 66 GF13 13% Glass Fiber Reinforced Nylon 66
- 3M Scotch® 8959 Bi-Directional Filament Tape
- Eastman Tenite Butyrate 465E3720008 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved