Huntsman Rexell® L8408 Cast Film Extrusion LLDPE  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman Rexell® L8408 Cast Film Extrusion LLDPE  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Linear-low density copolymer, high quality blown film extrusion, FDA compliant.Features: Excellent combination of sealability, mechanical strength optics, and very low gel levels.Applications: Sealing layer in coextruded films principally for food packaging and higher clarity films requiring very low gel levels.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 690 %
690 %
ASTM D882
Film Elongation at Break, TD >= 700 %
>= 700 %
ASTM D882
Secant Modulus, MD 0.172 GPa
24.9 ksi
ASTM D882
Secant Modulus, TD 0.186 GPa
27.0 ksi
ASTM D882
Elmendorf Tear Strength MD 460 g
460 g
ASTM D1922
Elmendorf Tear Strength TD 950 g
950 g
ASTM D1922
Elmendorf Tear Strength, MD 18.1 g/micron
460 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 37.4 g/micron
950 g/mil
ASTM D1922
Dart Drop 11.4 g/micron
290 g/mil
ASTM D1709
Dart Drop Test 290 g
0.639 lb
ASTM D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD >= 19.0 MPa
>= 2760 psi
ASTM D882
Optical Properties Metric English Comments
Haze 9.0 %
9.0 %
ASTM D1003
Gloss 66 %
66 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 205 - 245 °C
401 - 473 °F