Huntsman Rexell® L8102 Cast Film Extrusion LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Huntsman Rexell® L8102 Cast Film Extrusion LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Linear-low density copolymer with high slip and medium antiblock, general purpose blown film extrusion, FDA compliant.Features: Excellent combination of sealability, mechanical strength and optics.Applications: Sealing layer in coextruded films principally for food packaging.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	25.4 microns	1.00 mil
Melt Flow	1.0 g/10 min	1.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	>= 700 %	>= 700 %	ASTM D882
Secant Modulus, MD	0.138 GPa	20.0 ksi	ASTM D882
Secant Modulus, TD	0.159 GPa	23.1 ksi	ASTM D882
Elmendorf Tear Strength MD	360 g	360 g	ASTM D1922
Elmendorf Tear Strength TD	720 g	720 g	ASTM D1922
Elmendorf Tear Strength, MD	14.2 g/micron	360 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	28.3 g/micron	720 g/mil	ASTM D1922
Dart Drop	7.87 g/micron	200 g/mil	ASTM D1709
Dart Drop Test	200 g	0.441 lb	ASTM D1709
Film Tensile Strength at Break, MD	36.0 MPa	5220 psi	ASTM D882
Film Tensile Strength at Break, TD	>= 19.0 MPa	>= 2760 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	11 %	11 %	ASTM D1003
Gloss	60 %	60 %	at 45°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	205 - 245 °C	401 - 473 °F