Samsung Cheil Industries Starex® NH-1904 HIPS, Unreinforced FR

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® NH-1904 HIPS, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 52 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 52 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength, Yield 41.2 MPa
5970 psi
5 mm/min; ASTM D638
Elongation at Break 15 %
15 %
5 mm/min; ASTM D638
Flexural Strength 65.7 MPa
9530 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 0.785 J/cm

@Thickness 3.17 mm
 1.47 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C

@Thickness 6.40 mm
 174 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 95.0 °C
203 °F
B/50; ISO R306
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
V-0

@Thickness 2.50 mm
 V-0

@Thickness 0.0984 in