- Huntsman IROGRAN® CA116-201 TPU-Polyester
Huntsman IROGRAN® CA116-201 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® CA116-201 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN CA116-201 is a high performance polyester based thermoplastic polyurethane intended for flat die extrusion applications. IROGRAN CA116-201 is part of the HUNTSMAN film and sheet product range and offers a specially designed, flexible plasticizer free product suitable for the preparation of extruded films. Performance Features: Low melt temperature High crystallization rate Good low temperature flexibility Good processabilityApplications: Adhesive film Lamination Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Melt Index of Compound | 15 g/10 min @Load 5.00 kg, Temperature 190 °C |
15 g/10 min @Load 11.0 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 400 % | 400 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00607 GPa | 0.880 ksi | Injection molded parts; ASTM D412 |
| 300% Modulus | 0.00658 GPa | 0.954 ksi | Injection molded parts; ASTM D412 |
| Tear Strength | 92.9 kN/m | 530 pli | Injection molded parts; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 90.0 - 120 °C | 194 - 248 °F | TMA Melt Range |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 160 °C | 320 °F | Extrusion |
| Middle Barrel Temperature | 170 °C | 338 °F | Extrusion |
| Adapter Temperature | 170 °C | 338 °F | Extrusion |
| Die Temperature | 170 °C | 338 °F | Extrusion |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-MASK II ST Conductive Foil Tape
- SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Europe-Africa-Middle East)
- Permabond TA459 Toughened Acrylic Adhesive
- SABIC Innovative Plastics ULTEM 2100F PEI
- Sharadaa Ceramics Sharada LTM 0.4 Insulating Castable
- A. Schulman POLYBATCH™ U-0294-L Blowing Agent Concentrate Based In PE
- Diamond Polymers DIAMALOY ABSPC 750 HF ABS/PC Alloy, Non-Halogen, Flame Retardant
- Covestro Makrolon® ET2613 Polycarbonate
- Axiall 10852 Wire & Cable Flexible PVC
- Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced, Lubricated
Copyright © lookpolymers.com All Rights Reserved