Huntsman IROGRAN® A 92 E 4694 Polyester-Based TPU-Injection Extrusion Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 E 4694 Polyester-Based TPU-Injection Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 92 E 4694 is a thermoplastic special- polyester-polyurethane for injection moulding and extrusion applications. Additional characteristics of the product are flexibility and high mechanical resistance. Performance Features: Good melt flow High wear resistance High oil resistance Dynamically highly loadable Low-temperature flexibilityApplications: For the production of tooth belts, round cords profiles, technical parts.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D995 |
| Melt Index of Compound | 57 g/10 min @Load 10.0 kg, Temperature 210 °C |
57 g/10 min @Load 22.0 lb, Temperature 410 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 41 | 41 | ASTM D2240 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | DIN 53504 |
| Elongation at Break | 570 % | 570 % | ASTM D412 |
| 100% Modulus | 0.00820 GPa | 1.19 ksi | DIN 53504 |
| 300% Modulus | 0.0197 GPa | 2.86 ksi | DIN 53504 |
| Rebound | 32 % | 32 % | Bayshore; ASTM D2632 |
| Tear Strength | 137 kN/m | 780 pli | ASTM D624 |
| Abrasion | 35 | 35 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 23 % @Temperature 23.0 °C, Time 252000 sec |
23 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 - 190 °C | 320 - 374 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- MV Labs AU250 HAuBr4·xH2O Hydrogen tetrabromoaurate(III) hydrate
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 58 Shore A (discontinued **)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 1.0 PHR MBT
- Minelco Muscovite Mica
- A. Schulman POLYBATCH™ Poly White P80494PF Concentrate Based In Polypropylene
- Topas Advanced Polymers TOPAS® 8007D-61 Cyclic Olefin Copolymer (COC)
- EMS-Grivory Grivory® HTV-6H1 black 9205 PA6T/6I-GF60
- E-Polymers EFLEX® S2060 Transparent
- 3M 235 Photographic Tape
- Abatron Ferrobond-LH™ Steel-Filled, Structural Adhesive Putty; High Temperature Liquid
Copyright © lookpolymers.com All Rights Reserved