BASF Ultramid® 8202C HS BK-102 PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8202C HS BK-102 PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8202C HS BK-102 is a heat stabilized, low viscosity, pigmented black, PA6, injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in non-heat stabilized (Ultramid 8202C).
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 1.6 %
1.6 %
24 hour; ISO Test
9.3 %
9.3 %
ISO 62
Moisture Absorption at Equilibrium 2.6 %
2.6 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM Test
Tensile Strength, Yield 85.0 MPa
12300 psi
50mm/min; ISO 527
Elongation at Break 10 %
10 %
50mm/min, Nominal strain; ISO 527
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1mm/min; ISO 527
Flexural Strength 95.0 MPa
13800 psi
ISO Data
Flexural Modulus 2.80 GPa
406 ksi
ISO Data
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 81.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
45.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ISO 75
Flammability, UL94 V-2

@Thickness 0.700 mm
V-2

@Thickness 0.0276 in
V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Impact Modified No
Primary Processing Technique Injection Molding
UL.UL-C Yes