Huntsman IROGRAN® A 92 E 4246 Polyester-Based TPU-High Performance Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 E 4246 Polyester-Based TPU-High Performance Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 92 E 4246 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are short cycle times, good melt flow and easy demolding. Performance Features: Easy demolding Short cycle times High demolding stability High stability of melt High wear resistance Applications: For the production of buffers, seals, sprocket wheels, bearing shells.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 |
| Melt Index of Compound | 48 g/10 min @Load 21.6 kg, Temperature 210 °C |
48 g/10 min @Load 47.6 lb, Temperature 410 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | ASTM D2240 |
| Hardness, Shore D | 42 | 42 | ASTM D2240 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | DIN 53504 |
| Elongation at Break | 650 % | 650 % | ASTM D412 |
| 100% Modulus | 0.00720 GPa | 1.04 ksi | DIN 53504 |
| 300% Modulus | 0.0150 GPa | 2.18 ksi | DIN 53504 |
| Rebound | 32 % | 32 % | Bayshore; ASTM D2632 |
| Tear Strength | 89.4 kN/m | 510 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 175 - 190 °C | 347 - 374 °F | |
| 170 - 195 °C | 338 - 383 °F | Injection | |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Halar® 300LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (discontinued **)
- Iran Petrochemical (PCC) PET BG-821 Polyethylene Terephthalate
- Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F)
- SABIC Innovative Plastics ULTEM CRS5711 PEI (Asia Pacific)
- Samsung Cheil Industries Infino® XP-2140 PPS
- Master Bond Supreme 3HTND-2GT One Part, Toughened, Fast Curing Glob Top Adhesive
- Thermoseal Miliam Mica PPS 130 Laminate
- Buckeye Polymers BP RPP 2011 C Polypropylene, 20% Mineral Filled
- ArcelorMittal MartINsite® 1200 Cold Rolled Steel
- 3M 2E79 (Clear) Co-Extruded Protective Tape
Copyright © lookpolymers.com All Rights Reserved