Huntsman IROGRAN® A 85 P 4722 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 P 4722 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 85 P 4722 is a halogen-free thermoplastic- polyurethane for injection molding and extrusion applications. Additional characteristics of the product are good microbial resistance, high low-temperature flexibility, especially suitable for the substructure in cable construction. Performance Features: Good hydrolysis resistance Excellent processability Good abrasion resistance Halogen free Applications: For the production in jacket construction.Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | Injection molded parts |
| Melt Index of Compound | 100 g/10 min @Load 21.6 kg, Temperature 190 °C |
100 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | >= 35.0 MPa | >= 5080 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | >= 600 % | >= 600 % | Injection molded parts; DIN 53504 |
| Abrasion | <= 30 | <= 30 | mm<sup>3</sup>, Injection molded; ISO 4649 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ S212 High Performance Polypropylene Nanocomposite
- Pinnacle Polymers 2135 H Medium Impact Polypropylene Copolymer, Injection Molding Grade
- DuPont Bynel® 11E573 Modified EVA Adhesive Resin (discontinued **)
- Fainplast Compounds RH 306/W Rigid PVC, Antishock Extrusion
- Henkel Turco 6881 Paint Remover
- Solvay SUPRAGIL® GN 4-4’ Dihydroxydiphenyl Sulphonate Condensate Sodium Salt
- Borealis HB600TF Polypropylene
- Asahi Kasei Thermylene® P6-30FG-1734 30% Glass Fiber Reinforced, Heat Stabilized
- BASF Ultramid® A3ZG3 HP BK 20465 PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved