Huntsman IROGRAN® A 85 E 4607 E TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 E 4607 E TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 85 E 4607 is a thermoplastic polyether- polyurethane intended for extrusion and injection molding applications. Additional characteristics of the product are excellent mechanical properties and high tear strength. Performance Features: Good melt flow High wear resistance High elasticity Oil resistance Low-temperature flexibilityApplications: For the production of spiral hoses, tooth belts round cords, casual shoe solesInformation provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Injection molded; ASTM D955 |
| Melt Index of Compound | 35 g/10 min @Load 21.6 kg, Temperature 190 °C |
35 g/10 min @Load 47.6 lb, Temperature 374 °F |
MVR, [cm<sup>3</sup>/10 min] |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | Injection molded parts; ASTM D2240 |
| Hardness, Shore D | 34 | 34 | Injection molded parts; ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Injection molded parts; DIN 53504 |
| Elongation at Break | 650 % | 650 % | Injection molded parts; DIN 53504 |
| 100% Modulus | 0.00500 GPa | 0.725 ksi | Injection molded parts; DIN 53504 |
| 300% Modulus | 0.0140 GPa | 2.03 ksi | Injection molded parts; DIN 53504 |
| Tear Strength | 99.9 kN/m | 570 pli | Injection molded parts; ASTM D624 |
| Abrasion | 25 | 25 | mm<sup>3</sup>, Injection molded; ISO 4649 |
| Compression Set | 25 % @Temperature 22.8 °C, Time 86400 sec |
25 % @Temperature 73.0 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| 40 % @Temperature 70.0 °C, Time 86400 sec |
40 % @Temperature 158 °F, Time 24.0 hour |
Injection molded; ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Middle Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
Users viewing this material also viewed the following:
- Fiberfil® PP-60/FR Polypropylene Homopolymer, Flame Retardant, UL94 V0
- Garlock GYLON® 3545 Layered Microcellular PTFE Gasketing
- Solvay Specialty Polymers KetaSpire® KT-820 Polyetheretherketone (PEEK)
- Eagle Brass 194 HSM® Copper, Hard
- ConocoPhillips Syncon® 680 Synthetic EP Gear Oil, AGMA No. 8EP
- DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 50 Gauge
- Alliance Polymers Zythane™ 7045A Thermoplastic Polyurethane Elastomer
- Ineos Nova S-3201 Medium Impact Compact Polystyrene (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP PX01658 PA 6
Copyright © lookpolymers.com All Rights Reserved