- Goodfellow Polyaramid/Vinylester Composite Tube or Rod
Goodfellow Polyaramid/Vinylester Composite Tube or Rod
| Category | Polymer , Thermoset , Vinyl Ester |
| Manufacturer | Goodfellow |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Goodfellow Polyaramid/Vinylester Composite Tube or Rod.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Goodfellow.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 - 1.40 g/cc | 0.0434 - 0.0506 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 800 - 1000 MPa | 116000 - 145000 psi | Longitudinal |
| Elongation at Break | 2.5 % | 2.5 % | Longitudinal |
| Flexural Strength | 150 - 250 MPa | 21800 - 36300 psi | Longitudinal |
| Flexural Modulus | 17.0 - 22.0 GPa | 2470 - 3190 ksi | Longitudinal |
| Compressive Strength | 100 - 300 MPa | 14500 - 43500 psi | Longitudinal |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Volume Fraction Fibers, % | 50-60 |
Users viewing this material also viewed the following:
- Nilit Polynil® P100 Medium Viscosity Nylon 66
- Ineos Nova T243C Expandable Polystyrene
- Teknor Apex Sinpolene MBW1781 Linear Low Density Polyethylene
- Borealis RA130E-6017 Polypropylene Random Copolymer
- Dow Corning SYL-OFF® SL 160 COATING
- Braskem EB861 Blown Film Extrusion Low Density Polyethylene
- Aclo Accutech Polypropylene Homopolymer HP0339G20CL Glass Reinforced Coupled
- Aremco Graphi-Bond™ 551-RN High Temperature Ceramic Adhesive/Paste, Graphite Filled
- Solvay Specialty Polymers Veradel® A-304P Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved