Humiseal 1A20 Urethane Conformal Coating
| Category | Polymer , Adhesive , Thermoset , Polyurethane, TS , Thermoset Polyurethane, Adhesive |
| Manufacturer | Humiseal |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Humiseal 1A20 Urethane Conformal Coating.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Humiseal 1A20 Urethane Conformal CoatingHigh moisture resistanceExcellent dielectrical propertiesExcellent chemical resistanceRepairableUL ApprovedMIL-I-46058C ApprovedPasses thermal shock test (MIL-I-46058C)Flammability (self extinguishing) (ASTM D635)Excellent resistance to solvents (IPC CC 830)Recommended Stripper: 1071Recommended Thinner: 521 Cure Type: Room Temp or Heat
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0364 lb/in³ | ASTM D1475 |
| Solids Content | 50 % | 50 % | Fed Std 141 Method 4044 |
| Volatile Organic Compounds (VOC) Content | 510 g/l | 510 g/l | |
| Viscosity | 200 cP | 200 cP | Fed Std Method 4287 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 0.089590 GPa | 12.994 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 510 µm/m-°C @Temperature 20.0 °C |
283 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Minimum Service Temperature, Air | -65.0 °C | -85.0 °F | |
| Glass Transition Temp, Tg | 71.0 °C | 160 °F | |
| Flash Point | 28.3 °C | 83.0 °F | ASTM D56 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 4.80e+10 ohm | 4.80e+10 ohm | Moisture Resistance; MIL-I-46058C |
| Insulation Resistance | 3.00e+14 ohm | 3.00e+14 ohm | Insulation Resistance; MIL-I-46058C |
| Dielectric Constant | 3.5 | 3.5 | ASTM D1 50 65T |
| Dielectric Breakdown | >= 1500 V | >= 1500 V | Dielectric Withstand; MIL-I-46058C |
| Dissipation Factor | 0.028 | 0.028 | ASTM D1 50 65T |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min | 1.00 hour | Dry Time to Handling; Fed Std 141 4061 |
| 180 min @Temperature 170 °C |
3.00 hour @Temperature 338 °F |
||
| >= 1440 min @Temperature 23.0 °C |
>= 24.0 hour @Temperature 73.4 °F |
||
| Shelf Life | 6.00 Month @Temperature 23.0 °C |
6.00 Month @Temperature 73.4 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage | 375 ft²/gal |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 69 GF 45 PP, 45% glass fibre
- PlastiComp Complet® LBF50-PA66 50% Long Basalt Fiber
- Dielectric Polymers NT-2802 Ultra Tack Tape (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RFN18 PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Blue 40567 Concentrate Based In LDPE
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- ExxonMobil Mobil Almo 525
- Chosun Refractories GPB-1 Special brick
- Wanhua Chemical Wanthane® WHT-1590 Polyester Based TPU
Copyright © lookpolymers.com All Rights Reserved