Honeywell Capran® Oxyshield™ OXTR (Retortable Grade, 1.0 mil) Monoaxially Oriented Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ OXTR (Retortable Grade, 1.0 mil) Monoaxially Oriented Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Oxyshield™ Oriented Ultra Barrier Retortable Grade is a monoaxially oriented, co-extruded nylon 6-based clear film having excellent gas barrier through a broad range of relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 181 g/m²/day | 11.7 g/100 in²/day | 100°F (37.8°C) / 97%RH; ASTM F1249 |
| Oxygen Transmission Rate | 1.04 cc/m²/day | 0.0670 cc/100 in²/day | 73°F (23°F) / 65%RH; ASTM D3985 |
| 1.23 cc/m²/day | 0.0792 cc/100 in²/day | 73°F (23°C) / 0%RH; ASTM D3985 | |
| Thickness | 25.4 microns | 1.00 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 87 % | 87 % | ASTM D882 |
| Film Elongation at Break, TD | 413 % | 413 % | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | film to stainless steel; ASTM D1894 |
| 0.50 | 0.50 | film to film; ASTM D1894 | |
| Tear Strength Test | 732 | 732 | graves tear MD, grams/mil; ASTM D1004 |
| 1192 | 1192 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 241 MPa | 35000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 99.3 MPa | 14400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | <= 93.0 °C | <= 199 °F | continuous use temperature |
| <= 176 °C | <= 349 °F | short time use temperature | |
| Shrinkage, MD | 11 % | 11 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | 1.6 % | 1.6 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 5.5 % | <= 5.5 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 W-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
- Reliance Industries Repol H029SG Polypropylene
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 17% Plasticizer (discontinued **)
- Hong Kun Group N-Trityl-L-serine Methyl Ester Pharmaceutical Intermediate
- Kennametal Stellite Stellite® 19
- Materion Beryllium Copper Alloy 25 Strip; 1/2H (TD02) Temper (UNS C17200)
- Ensinger Tecamid® 6/6 Nylon (PA66)
- Arkema Group Lacovyl® PE 1801 H PVC
- DSM Arnite® TV4 460 KL PBT/PET Blend-30% Glass Reinforced (European Grade)
Copyright © lookpolymers.com All Rights Reserved