Honeywell Capran® Emblem™ 1200M Bi-Axially Oriented Nylon 6 Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 1200M Bi-Axially Oriented Nylon 6 Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 1200M is a 0.48 mil (12 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adhesives. Metallization adhesion is excellent when using "M" coated products. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 357 - 403 g/m²/day | 23.0 - 26.0 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 54.0 - 70.0 cc/m²/day | 3.48 - 4.51 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 12.2 microns | 0.480 mil | |
| Surface Tension | >= 50 dynes/cm | >= 50 dynes/cm | untreated side; ASTM D5946 |
| >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D5946 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.413 - 3.916 GPa | 350.0 - 568.0 ksi | ASTM D882 |
| Secant Modulus, TD | 2.482 - 3.585 GPa | 360.0 - 520.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.17 - 0.28 | 0.17 - 0.28 | film to stainless steel; ASTM D1894 |
| 0.55 - 0.74 | 0.55 - 0.74 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear MD, grams/mil; ASTM D1004 |
| 1100 - 1500 | 1100 - 1500 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 234 - 303 MPa | 34000 - 44000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 193 - 303 MPa | 28000 - 44000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.5 % | 1.6 - 2.5 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.0 % | <= 3.0 % | ASTM D1003 |
| Gloss | 160 - 180 % | 160 - 180 % | at 20° |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Rigid Extrusion L0248 Polyvinyl Chloride, Rigid (PVC, Rigid)
- PTS Trimid® N66-G13L 13% Glass Fiber Reinforced Lubed Nylon 6/6
- Michelman® Michem® Lube 160F Anionic carnauba wax emulsion
- Solvay Specialty Polymers Polidan® S/I 20 Polyethylene, Crosslinked (XLPE)
- Techmer ES HiFill® PA6/6 GF30 HS L 30% Glass Filled
- Shandong Dongyue Polymer DF-17 PTFE Molding Powder (Micronized Particles)
- Universal Wire Works 60 Nickel Alloy Welding Wire
- A. Schulman POLYTROPE™ TPP 1010-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- DuPont Performance Polymers Hytrel® 5526 Polyester Elastomer TPC-ET (Unverified Data**)
- PlastxWorld CEVIAN® SER23 ABS
Copyright © lookpolymers.com All Rights Reserved