- Aremco Ceramacast™ 586 High Temperature Potting & Casting Material Zirconia Silicate
Aremco Ceramacast™ 586 High Temperature Potting & Casting Material Zirconia Silicate
| Category | Ceramic , Oxide , Silicon Oxide , Zirconium Oxide , Potting/Casting Ceramic |
| Manufacturer | Aremco |
| Trade Name | Ceramacast™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramacast™ 586 High Temperature Potting & Casting Material Zirconia Silicate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Castable ceramic for ceramic and metal assemblies. Excellent handling, fast curing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 1.68 g/cc | 0.0608 lb/in³ | Powder |
| Porosity | <= 2.0 % | <= 2.0 % | |
| pH | 2.0 - 3.0 | 2.0 - 3.0 | |
| Viscosity | 15000 cP | 15000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | 55.2 MPa | 8000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.86 µm/m-°C @Temperature 20.0 °C |
2.70 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 1540 °C | 2800 °F | |
| Shrinkage | <= 0.300 % @Temperature 538 °C |
<= 0.300 % @Temperature 1000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Dielectric Strength | 4.92 kV/mm | 125 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Dry Time | >= 8 hour | >= 8 hour | Air dry |
| Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
| Pot Life | 60 - 120 min | 60 - 120 min | |
| Shelf Life | 12.0 Month | 12.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | |
| Alkali Resistance | Good | |
| Color | Off White | |
| Mix Ratio | 100:13-15 | |
| Moisture Resistance | Good |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP 9X06483 PA 46
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 18% Plasticizer (discontinued **)
- Michelman® Nomar® 70THIN Non-abrasive paper coating
- Latrobe Cascadeâ„¢ P21 Prehardened Die Steel (AISI P21)
- Sylvin Technologies 9950-85 Natural PVC Molding Compound
- DSM Stanyl® TW250F6 Nylon 46-30% Glass Reinforced (European Grade) (Dry)
- Fainplast Compounds HAX HF 22G Halogen Free PVC
- C.O.I.M. LARIPUR® LPR70D60 PTMG Polyether Polyurethane
- Unifrax Fiberfrax® QF-150™ Coating Cement
- DuPont™ Surlyn® 1706 Zinc Ionomer
Copyright © lookpolymers.com All Rights Reserved