Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Haynes Ultimet® alloy, 6.3-38.1 mm plate

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name Ultimet®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Ultimet® alloy, 6.3-38.1 mm plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptional ductility and resistance to weld cracking, very easy to apply as an overlay, multiple layers appliable with little to no preheat. Applications include agitators, blenders, bolts, dies, extruders, fan blades, filters, glass plungers, nozzles, pumps, rolls, screw conveyors, and valve parts.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.47 g/cc
0.306 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1020 MPa
148000 psi
214 MPa

@Temperature 982 °C
 31000 psi

@Temperature 1800 °F
352 MPa

@Temperature 871 °C
 51100 psi

@Temperature 1600 °F
524 MPa

@Temperature 760 °C
 76000 psi

@Temperature 1400 °F
683 MPa

@Temperature 649 °C
 99100 psi

@Temperature 1200 °F
862 MPa

@Temperature 538 °C
 125000 psi

@Temperature 1000 °F
917 MPa

@Temperature 427 °C
 133000 psi

@Temperature 801 °F
952 MPa

@Temperature 316 °C
 138000 psi

@Temperature 601 °F
986 MPa

@Temperature 93.0 °C
 143000 psi

@Temperature 199 °F
986 MPa

@Temperature 204 °C
 143000 psi

@Temperature 399 °F
Tensile Strength, Yield 545 MPa

@Strain 0.200 %
 79000 psi

@Strain 0.200 %
110 MPa

@Strain 0.200 %,
Temperature 982 °C
 16000 psi

@Strain 0.200 %,
Temperature 1800 °F
193 MPa

@Strain 0.200 %,
Temperature 871 °C
 28000 psi

@Strain 0.200 %,
Temperature 1600 °F
255 MPa

@Strain 0.200 %,
Temperature 649 °C
 37000 psi

@Strain 0.200 %,
Temperature 1200 °F
262 MPa

@Strain 0.200 %,
Temperature 538 °C
 38000 psi

@Strain 0.200 %,
Temperature 1000 °F
269 MPa

@Strain 0.200 %,
Temperature 760 °C
 39000 psi

@Strain 0.200 %,
Temperature 1400 °F
310 MPa

@Strain 0.200 %,
Temperature 427 °C
 45000 psi

@Strain 0.200 %,
Temperature 801 °F
331 MPa

@Strain 0.200 %,
Temperature 316 °C
 48000 psi

@Strain 0.200 %,
Temperature 601 °F
379 MPa

@Strain 0.200 %,
Temperature 204 °C
 55000 psi

@Strain 0.200 %,
Temperature 399 °F
483 MPa

@Strain 0.200 %,
Temperature 93.0 °C
 70100 psi

@Strain 0.200 %,
Temperature 199 °F
Elongation at Break 36 %
36 %
in 50.8 mm
40 %

@Temperature 93.0 °C
 40 %

@Temperature 199 °F
 in 50.8 mm
61 %

@Temperature 204 °C
 61 %

@Temperature 399 °F
 in 50.8 mm
66 %

@Temperature 649 °C
 66 %

@Temperature 1200 °F
 in 50.8 mm
70 %

@Temperature 760 °C
 70 %

@Temperature 1400 °F
 in 50.8 mm
70 %

@Temperature 316 °C
 70 %

@Temperature 601 °F
 in 50.8 mm
70 %

@Temperature 427 °C
 70 %

@Temperature 801 °F
 in 50.8 mm
70 %

@Temperature 538 °C
 70 %

@Temperature 1000 °F
 in 50.8 mm
77 %

@Temperature 871 °C
 77 %

@Temperature 1600 °F
 in 50.8 mm
100 %

@Temperature 982 °C
 100 %

@Temperature 1800 °F
 in 50.8 mm
Modulus of Elasticity 180 GPa

@Temperature 649 °C
 26100 ksi

@Temperature 1200 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
189 GPa

@Temperature 538 °C
 27400 ksi

@Temperature 1000 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
197 GPa

@Temperature 427 °C
 28600 ksi

@Temperature 801 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
206 GPa

@Temperature 316 °C
 29900 ksi

@Temperature 601 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
215 GPa

@Temperature 204 °C
 31200 ksi

@Temperature 399 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
Charpy Impact 176 J

@Temperature 23.0 °C
 130 ft-lb

@Temperature 73.4 °F
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature 26.0 - 316 °C
 7.78 µin/in-°F

@Temperature 78.8 - 601 °F
14.5 µm/m-°C

@Temperature 26.0 - 427 °C
 8.06 µin/in-°F

@Temperature 78.8 - 801 °F
14.8 µm/m-°C

@Temperature 26.0 - 538 °C
 8.22 µin/in-°F

@Temperature 78.8 - 1000 °F
15.1 µm/m-°C

@Temperature 26.0 - 649 °C
 8.39 µin/in-°F

@Temperature 78.8 - 1200 °F
15.9 µm/m-°C

@Temperature 26.0 - 760 °C
 8.83 µin/in-°F

@Temperature 78.8 - 1400 °F
16.4 µm/m-°C

@Temperature 26.0 - 871 °C
 9.11 µin/in-°F

@Temperature 78.8 - 1600 °F
16.9 µm/m-°C

@Temperature 26.0 - 982 °C
 9.39 µin/in-°F

@Temperature 78.8 - 1800 °F
Specific Heat Capacity 0.456 J/g-°C

@Temperature 23.0 °C
 0.109 BTU/lb-°F

@Temperature 73.4 °F
0.470 J/g-°C

@Temperature 100 °C
 0.112 BTU/lb-°F

@Temperature 212 °F
0.482 J/g-°C

@Temperature 200 °C
 0.115 BTU/lb-°F

@Temperature 392 °F
0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
0.525 J/g-°C

@Temperature 400 °C
 0.125 BTU/lb-°F

@Temperature 752 °F
0.545 J/g-°C

@Temperature 500 °C
 0.130 BTU/lb-°F

@Temperature 932 °F
0.573 J/g-°C

@Temperature 600 °C
 0.137 BTU/lb-°F

@Temperature 1110 °F
Thermal Conductivity 12.3 W/m-K

@Temperature 23.0 °C
 85.4 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
13.8 W/m-K

@Temperature 100 °C
 95.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
15.6 W/m-K

@Temperature 200 °C
 108 BTU-in/hr-ft²-°F

@Temperature 392 °F
17.5 W/m-K

@Temperature 300 °C
 121 BTU-in/hr-ft²-°F

@Temperature 572 °F
19.4 W/m-K

@Temperature 400 °C
 135 BTU-in/hr-ft²-°F

@Temperature 752 °F
21.5 W/m-K

@Temperature 500 °C
 149 BTU-in/hr-ft²-°F

@Temperature 932 °F
23.9 W/m-K

@Temperature 600 °C
 166 BTU-in/hr-ft²-°F

@Temperature 1110 °F
Melting Point 1332 - 1354 °C
2430 - 2469 °F
Solidus 1332 °C
2430 °F
Liquidus 1354 °C
2469 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000870 ohm-cm

@Temperature 23.0 °C
 0.0000870 ohm-cm

@Temperature 73.4 °F
0.0000890 ohm-cm

@Temperature 100 °C
 0.0000890 ohm-cm

@Temperature 212 °F
0.0000930 ohm-cm

@Temperature 200 °C
 0.0000930 ohm-cm

@Temperature 392 °F
0.0000960 ohm-cm

@Temperature 300 °C
 0.0000960 ohm-cm

@Temperature 572 °F
0.000100 ohm-cm

@Temperature 400 °C
 0.000100 ohm-cm

@Temperature 752 °F
0.000103 ohm-cm

@Temperature 500 °C
 0.000103 ohm-cm

@Temperature 932 °F
0.000105 ohm-cm

@Temperature 600 °C
 0.000105 ohm-cm

@Temperature 1110 °F
Users viewing this material also viewed the following: