- PolyOne Edgetek® PS-30GF/000 FR V0 Polybutylene Terephthalate (PBT), Glass Filled (discontinued **)
PolyOne Edgetek® PS-30GF/000 FR V0 Polybutylene Terephthalate (PBT), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® PS-30GF/000 FR V0 Polybutylene Terephthalate (PBT), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedFlame RetardantPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Water Absorption | 0.070 % | 0.070 % | 24 hr. Immersion, -; ASTM D570 |
| 0.45 % | 0.45 % | Long-Term Immersion, -; ASTM D570 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 121 MPa | 17500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Compressive Strength | 131 MPa | 19000 psi | ASTM D695 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.80 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 249 °C | 450 - 480 °F | Molding |
| Mold Temperature | 93.3 - 107 °C | 200 - 225 °F | |
| Drying Temperature | 107 °C | 225 °F | 4 hrs |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL4019 PC
- Arkema Group Oroglas® MI-4T Acrylic, Heat Resistant (discontinued **)
- SABIC Innovative Plastics LNP COLORCOMP E1000 PEI (Europe-Africa-Middle East)
- A. Schulman FORMION™ FI 394 Ionomer
- Elektro-Isola Etronax MF Phenolic, Cotton Fabric Reinforcement, Brown, Sheets
- Arkema Group LOTADER® 4720 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- Nye Lubricants 795LT (NG) Synthetic Oil
- UBE B (Low-Cis) HIPS (n-DM =0.03 wt %)
- Plaskolite West Optix® CA - 75 OG General Purpose Acrylic Resin
- Gwent Electronic Materials C2000802P2 Carbon Graphite Ink
Copyright © lookpolymers.com All Rights Reserved