Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications include afterburner parts and nozzle diaphragm partitions in current gas turbine engines. Formed with success on drop-hammers, expanding mandrels and stretch formers.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.25 g/cc
0.298 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1285 MPa
186400 psi
75.0 MPa

@Temperature 1093 °C
 10900 psi

@Temperature 1999 °F
274 MPa

@Temperature 982 °C
 39700 psi

@Temperature 1800 °F
702 MPa

@Temperature 871 °C
 102000 psi

@Temperature 1600 °F
996 MPa

@Temperature 760 °C
 144000 psi

@Temperature 1400 °F
1128 MPa

@Temperature 649 °C
 163600 psi

@Temperature 1200 °F
1136 MPa

@Temperature 538 °C
 164800 psi

@Temperature 1000 °F
Tensile Strength, Yield 1024 MPa

@Strain 0.200 %
 148500 psi

@Strain 0.200 %
38.0 MPa

@Strain 0.200 %,
Temperature 1093 °C
 5510 psi

@Strain 0.200 %,
Temperature 1999 °F
169 MPa

@Strain 0.200 %,
Temperature 982 °C
 24500 psi

@Strain 0.200 %,
Temperature 1800 °F
538 MPa

@Strain 0.200 %,
Temperature 871 °C
 78000 psi

@Strain 0.200 %,
Temperature 1600 °F
825 MPa

@Strain 0.200 %,
Temperature 760 °C
 120000 psi

@Strain 0.200 %,
Temperature 1400 °F
890 MPa

@Strain 0.200 %,
Temperature 649 °C
 129000 psi

@Strain 0.200 %,
Temperature 1200 °F
927 MPa

@Strain 0.200 %,
Temperature 538 °C
 134000 psi

@Strain 0.200 %,
Temperature 1000 °F
Elongation at Break 14 %
14 %
in 50.8 mm
5.0 %

@Temperature 871 °C
 5.0 %

@Temperature 1600 °F
 in 50.8 mm
6.0 %

@Temperature 760 °C
 6.0 %

@Temperature 1400 °F
 in 50.8 mm
8.0 %

@Temperature 649 °C
 8.0 %

@Temperature 1200 °F
 in 50.8 mm
14 %

@Temperature 538 °C
 14 %

@Temperature 1000 °F
 in 50.8 mm
15 %

@Temperature 982 °C
 15 %

@Temperature 1800 °F
 in 50.8 mm
47 %

@Temperature 1093 °C
 47 %

@Temperature 1999 °F
 in 50.8 mm
Modulus of Elasticity 222 GPa
32200 ksi
112 GPa

@Temperature 982 °C
 16200 ksi

@Temperature 1800 °F
120 GPa

@Temperature 871 °C
 17400 ksi

@Temperature 1600 °F
133 GPa

@Temperature 760 °C
 19300 ksi

@Temperature 1400 °F
162 GPa

@Temperature 649 °C
 23500 ksi

@Temperature 1200 °F
165 GPa

@Temperature 538 °C
 23900 ksi

@Temperature 1000 °F
Poissons Ratio 0.31
0.31
27°C (80°F)
0.31

@Temperature 149 °C
 0.31

@Temperature 300 °F
0.32

@Temperature 482 °C
 0.32

@Temperature 900 °F
0.32

@Temperature 371 °C
 0.32

@Temperature 700 °F
0.32

@Temperature 260 °C
 0.32

@Temperature 500 °F
0.33

@Temperature 760 °C
 0.33

@Temperature 1400 °F
0.33

@Temperature 677 °C
 0.33

@Temperature 1250 °F
0.33

@Temperature 649 °C
 0.33

@Temperature 1200 °F
0.34

@Temperature 843 °C
 0.34

@Temperature 1550 °F
0.35

@Temperature 927 °C
 0.35

@Temperature 1700 °F
Shear Modulus 83.0 GPa
12000 ksi
27°C
55.0 GPa

@Temperature 927 °C
 7980 ksi

@Temperature 1700 °F
61.0 GPa

@Temperature 843 °C
 8850 ksi

@Temperature 1550 °F
64.0 GPa

@Temperature 760 °C
 9280 ksi

@Temperature 1400 °F
67.0 GPa

@Temperature 677 °C
 9720 ksi

@Temperature 1250 °F
69.0 GPa

@Temperature 593 °C
 10000 ksi

@Temperature 1100 °F
72.0 GPa

@Temperature 482 °C
 10400 ksi

@Temperature 900 °F
75.0 GPa

@Temperature 371 °C
 10900 ksi

@Temperature 700 °F
77.0 GPa

@Temperature 260 °C
 11200 ksi

@Temperature 500 °F
81.0 GPa

@Temperature 149 °C
 11700 ksi

@Temperature 300 °F
Thermal Properties Metric English Comments
CTE, linear 13.5 µm/m-°C

@Temperature 21.0 - 538 °C
 7.50 µin/in-°F

@Temperature 69.8 - 1000 °F
14.0 µm/m-°C

@Temperature 21.0 - 649 °C
 7.78 µin/in-°F

@Temperature 69.8 - 1200 °F
14.8 µm/m-°C

@Temperature 21.0 - 760 °C
 8.22 µin/in-°F

@Temperature 69.8 - 1400 °F
15.2 µm/m-°C

@Temperature 21.0 - 871 °C
 8.44 µin/in-°F

@Temperature 69.8 - 1600 °F
16.3 µm/m-°C

@Temperature 21.0 - 927 °C
 9.06 µin/in-°F

@Temperature 69.8 - 1700 °F
16.8 µm/m-°C

@Temperature 21.0 - 982 °C
 9.33 µin/in-°F

@Temperature 69.8 - 1800 °F
Specific Heat Capacity 0.452 J/g-°C

@Temperature 21.0 °C
 0.108 BTU/lb-°F

@Temperature 69.8 °F
Thermal Conductivity 11.5 W/m-K

@Temperature 149 °C
 79.8 BTU-in/hr-ft²-°F

@Temperature 300 °F
12.5 W/m-K

@Temperature 204 °C
 86.8 BTU-in/hr-ft²-°F

@Temperature 399 °F
13.6 W/m-K

@Temperature 260 °C
 94.4 BTU-in/hr-ft²-°F

@Temperature 500 °F
14.7 W/m-K

@Temperature 316 °C
 102 BTU-in/hr-ft²-°F

@Temperature 601 °F
16.8 W/m-K

@Temperature 427 °C
 117 BTU-in/hr-ft²-°F

@Temperature 801 °F
18.8 W/m-K

@Temperature 538 °C
 130 BTU-in/hr-ft²-°F

@Temperature 1000 °F
20.0 W/m-K

@Temperature 593 °C
 139 BTU-in/hr-ft²-°F

@Temperature 1100 °F
21.0 W/m-K

@Temperature 644 °C
 146 BTU-in/hr-ft²-°F

@Temperature 1190 °F
22.0 W/m-K

@Temperature 704 °C
 153 BTU-in/hr-ft²-°F

@Temperature 1300 °F
23.1 W/m-K

@Temperature 760 °C
 160 BTU-in/hr-ft²-°F

@Temperature 1400 °F
24.1 W/m-K

@Temperature 816 °C
 167 BTU-in/hr-ft²-°F

@Temperature 1500 °F
25.1 W/m-K

@Temperature 871 °C
 174 BTU-in/hr-ft²-°F

@Temperature 1600 °F
Melting Point 1310 - 1345 °C
2390 - 2453 °F
Solidus 1310 °C
2390 °F
Liquidus 1335 °C
2435 °F
Component Elements Properties Metric English Comments
Aluminum, Al 1.4 - 1.6 %
1.4 - 1.6 %
Electrical Properties Metric English Comments
Magnetic Permeability <= 1.002

@Temperature 21.0 °C
 <= 1.002

@Temperature 69.8 °F
 200 Oersted